Electret properties of polyetherimides:: Influence of water content and comparison with other high-temperature polymer films

被引：14

作者：

Frese, Thomas ^{[1
]}

Lovera, Deliani ^{[1
]}

Sandler, Jan K. W. ^{[1
]}

Lim, Goy Teck ^{[1
]}

Altstaedt, Volker ^{[1
]}

Giesa, Reiner ^{[1
]}

Schmidt, Hans-Werner ^{[1
]}

机构：

[1] Univ Bayreuth, Bayreuther Inst Makromol Forsch, D-95440 Bayreuth, Germany

来源：

MACROMOLECULAR MATERIALS AND ENGINEERING | 2007年 / 292卷 / 05期

关键词：

electrets; high performance polymers; high temperature materials; polyetherimide; polyimide; water absorption;

D O I：

10.1002/mame.200600463

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this comparative study, the charge storage performance of commercial high-temperature polymer films was evaluated and correlated with their chemical structure. Isothermal surface potential decay measurements after annealing periods at 90 degrees C revealed that amorphous polyetherimide (PEI) films showed the best charge storage behavior. Polyimide films showed reduced charge storage performance, whereas sulfur-containing polymer films are not suitable as electrets due to their fast charge decay. Additionally, the effect of water content in PEI films in the range of 0.02-0.79 wt.-% was studied. Increasing amounts of water decreased the charge storage properties proportionally, but only by a relatively, smaller amount: the highest investigated water content of 0.79 wt.-% reduced the charge by only 30%.

引用

页码：582 / 587

页数：6

共 33 条

[1] Morphology and electret behaviour of microcellular high glass temperature films [J].

Behrendt, N. ;

Greiner, C. ;

Fischer, F. ;

Frese, T. ;

Altstaedt, V. ;

Schmidt, H. -W. ;

Giesa, R. ;

Hillenbrand, J. ;

Sessler, G. M. .

APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2006, 85 (01) :87-93

[2] Charge storage behavior of isotropic and biaxially-oriented polypropylene films containing α- and β-nucleating agents [J].

Behrendt, N ;

Mohmeyer, N ;

Hillenbrand, J ;

Klaiber, M ;

Zhang, XQ ;

Sessler, GM ;

Schmidt, HW ;

Altstädt, V .

JOURNAL OF APPLIED POLYMER SCIENCE, 2006, 99 (03) :650-658

[3]

Boland J, 2003, PROC IEEE MICR ELECT, P538

[4]

DOMININGHAUS H, 2005, KUNSTSTOFFE IHRE EIG, P1156

[5] Generation of polymer electrets in a low-temperature glow-discharge plasma [J].

Drachev, AI .

HIGH ENERGY CHEMISTRY, 2003, 37 (05) :297-302

[6]

FROMMER JE, 1990, CONCISE ENCY POLYM S, P298

[7] CALLUS FORMATION BY ELECTRET [J].

FUKADA, E ;

TAKAMATSU, T ;

YASUDA, I .

JAPANESE JOURNAL OF APPLIED PHYSICS, 1975, 14 (12) :2079-2080

[8]

FUKUZAWA M, 2003, POLYM OTHER HIGH TEM, P255

[9] CONSTANT CURRENT CORONA TRIODE WITH GRID VOLTAGE CONTROL - APPLICATION TO POLYMER FOIL CHARGING [J].

GIACOMETTI, JA ;

CAMPOS, JSC .

REVIEW OF SCIENTIFIC INSTRUMENTS, 1990, 61 (03) :1143-1150

[10]

Giesa R., 2001, ENCY MAT SCI TECHNOL, P3803, DOI [10.1016/b0-08-043152-6/00677, DOI 10.1016/B0-08-043152-6/00677]

← 1 2 3 4 →