Simulation of Texture Evolution during Uniaxial Deformation of Commercially Pure Titanium

被引:6
作者
Bishoyi, B. [1 ]
Debta, M. K. [1 ]
Yadav, S. K. [1 ]
Sabat, R. K. [2 ]
Sahoo, S. K. [1 ]
机构
[1] NIT Rourkela, Dept Met & Mat Engn, Rourkela 769008, Odisha, India
[2] IISc Bangalore, Dept Mat Engn, Bangalore 560012, Karnataka, India
来源
7TH NATIONAL CONFERENCE ON PROCESSING AND CHARACTERIZATION OF MATERIALS (NCPCM 2017) | 2018年 / 338卷
关键词
Tension; Compression; Texture; EBSD; XRD; VPSC; MICROSTRUCTURE; TEMPERATURE;
D O I
10.1088/1757-899X/338/1/012038
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The evolution of texture in commercially pure (CP) titanium during uniaxial tension and compression through VPSC (Visco-plastic self-consistent) simulation is reported in the present study. CP-titanium was subjected to both uniaxial tension and compression upto 35% deformation. During uniaxial tension, tensile twin of {10 (1) over bar2}<<(1)over bar>011> type and compressive twin of {11 (2) over bar2}<11<(2)over bar>(3) over bar >type were observed in the samples. However, only tensile twin of {10 (1) over bar2}<<(1)over bar>011> type was observed in the samples during uniaxial compression. Volume fractions of the twins were increased linearly as a function of percentage deformation during uniaxial tension. Whereas, during uniaxial compression the twinning volume fraction was increased up to 20% deformation and then decreased rapidly on further increasing the percentage deformation. During uniaxial tension, the general t-type textures were observed in the samples irrespective of the percentage deformation. The initial non-basal texture was oriented to split basal texture during uniaxial compression of the sample. VPSC formulation was used for simulating the texture development in the material. Different hardening parameters were estimated through correlating the simulated stress-strain curve with the experimental stress-strain data. It was observed that, prismatic slip {10 (1) over bar0}<11<(2)over bar>0> operated as the primary deformation mode during uniaxial tension whereas basal slip {0001}<11<(2)over bar>0> acquired the leading role during deformation through uniaxial compression. It was also revealed that active deformation modes were fully depending on percentage deformation, loading direction, and orientation of grains.
引用
收藏
页数:6
相关论文
共 16 条
[11]   Strain hardening of titanium: role of deformation twinning [J].
Salem, AA ;
Kalidindi, SR ;
Doherty, RD .
ACTA MATERIALIA, 2003, 51 (14) :4225-4237
[12]   THE RELATION BETWEEN MACROSCOPIC AND MICROSCOPIC STRAIN-HARDENING IN FCC POLYCRYSTALS [J].
TOME, C ;
CANOVA, GR ;
KOCKS, UF ;
CHRISTODOULOU, N ;
JONAS, JJ .
ACTA METALLURGICA, 1984, 32 (10) :1637-1653
[13]   Mechanics of the ductile form changes of crystals [J].
von Mises, R .
ZEITSCHRIFT FUR ANGEWANDTE MATHEMATIK UND MECHANIK, 1928, 8 :161-185
[14]   Evaluation of self-consistent polycrystal plasticity models for magnesium alloy AZ31B sheet [J].
Wang, H. ;
Raeisinia, B. ;
Wu, P. D. ;
Agnew, S. R. ;
Tome, C. N. .
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2010, 47 (21) :2905-2917
[15]   Microstructure evolution of titanium after tensile test [J].
Wronski, S. ;
Wierzbanowski, K. ;
Jcdrychowski, M. ;
Tarasiuk, J. ;
Wronski, M. ;
Baczmanski, A. ;
Bacroix, B. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 656 :1-11
[16]   Role of deformation twin on texture evolution in cold-rolled commercial-purity Ti [J].
Zhong, Yong ;
Yin, Fuxing ;
Nayai, Kotobu .
JOURNAL OF MATERIALS RESEARCH, 2008, 23 (11) :2954-2966