Promotion of the mechanical properties and thermal conductivity of epoxy by low Si3N4 whisker content and its mechanisms

被引:12
作者
Liu, Xuan [1 ]
Zhang, Dian [1 ,2 ]
Liu, Yijun [3 ]
Liu, Jing [1 ]
Yang, Xiaofeng [1 ]
Gao, Yunqin [1 ]
Ma, Aiqiong [1 ]
机构
[1] Xian Univ Architecture & Technol, Coll Mat Sci & Engn, Xian 710055, Shaanxi, Peoples R China
[2] Sinosteel Luoyang Inst Refractories Res Co Ltd, State Key Lab Adv Refractories, Luoyang 471039, Henan, Peoples R China
[3] Monalisa Grp Co Ltd, Foshan 528211, Guangdong, Peoples R China
关键词
applications; composites; mechanical properties; packaging; SILANE COUPLING AGENTS; FRACTURE-TOUGHNESS; TOUGHENED EPOXY; FILLED EPOXY; MATRIX COMPOSITE; ALUMINUM NITRIDE; BORON-NITRIDE; NANOCOMPOSITES; SIZE; MICROSTRUCTURE;
D O I
10.1002/app.48721
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Si3N4 whisker (Si3N4w) is selected as epoxy filler. The influence of filler content on the bulk density, porosity, bending strength, Young's modulus, critical stress intensity factor, work of failure, morphologies of fracture surface, and thermal conductivity of Si3N4w/epoxy is investigated. The bending strength is 82.63 MPa at a Si3N4w content of 5 vol% and increases to 25.29% more than that of neat epoxy. Compared with that of neat epoxy, the work of failure and thermal conductivity increase by 455% and 34.78% to 18 248.92 J center dot m(-2) and 0.31 W center dot m(-1)center dot K-1, respectively, at a Si3N4w content of 7 vol%. However, Si3N4w/epoxy becomes sensitive to precrack due to a weak C-N bond and residual tensile stress at the interface, thereby resulting in the decline of critical stress intensity factor. The coexistence of various energy dissipation mechanisms, namely, steps, craters or depressions, stress whitening, plastic flow, pull out of Si3N4w, and rough fracture surface, is observed in Si3N4w/epoxy. (c) 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019, 137, 48721.
引用
收藏
页数:11
相关论文
共 49 条
[1]   Thermal Conductivity of Polymer Nanocomposites Made With Carbon Nanofibers [J].
Agarwal, Sushant ;
Khan, M. Masud K. ;
Gupta, Rakesh K. .
POLYMER ENGINEERING AND SCIENCE, 2008, 48 (12) :2474-2481
[2]   Preparation of waterborne epoxy dispersion and its application in 2K waterborne epoxy coatings [J].
Ai, Dan ;
Mo, Ruibin ;
Wang, Huihui ;
Lai, Yingbiao ;
Jiang, Xiang ;
Zhang, Xinya .
PROGRESS IN ORGANIC COATINGS, 2019, 136
[3]   Carbon fiber/epoxy matrix composite interphases modified with cellulose nanocrystals [J].
Batista, Mariana Desiree Reale ;
Drzal, Lawrence T. .
COMPOSITES SCIENCE AND TECHNOLOGY, 2018, 164 :274-281
[4]   Fracture toughness and failure mechanism of graphene based epoxy composites [J].
Chandrasekaran, Swetha ;
Sato, Narumichi ;
Toelle, Folke ;
Muelhaupt, Rolf ;
Fiedler, Bodo ;
Schulte, Karl .
COMPOSITES SCIENCE AND TECHNOLOGY, 2014, 97 :90-99
[5]   FRACTURE OF SHEAR BANDS IN ATACTIC POLYSTYRENE [J].
CHAU, CC ;
LI, JCM .
JOURNAL OF MATERIALS SCIENCE, 1981, 16 (07) :1858-1873
[6]   Dispersion stability of Si3N4 nano-particles modified by γ-methacryloxypropyl trimethoxy silane (MAPTMS) in organic solvent [J].
Cheng, Guojun ;
Qian, Jiasheng ;
Tang, Zhongfeng ;
Ding, Guoxin ;
Zhu, Jinbo .
CERAMICS INTERNATIONAL, 2015, 41 (01) :1879-1884
[7]   Immobilization of lipase on a polymeric microsphere with an epoxy group prepared by radiation-induced polymerization [J].
Choi, SH ;
Lee, KP ;
Kang, HD .
JOURNAL OF APPLIED POLYMER SCIENCE, 2003, 88 (05) :1153-1161
[8]   Effect of silica nanoparticle size on toughening mechanisms of filled epoxy [J].
Dittanet, Peerapan ;
Pearson, Raymond A. .
POLYMER, 2012, 53 (09) :1890-1905
[9]   Boron nitride filled epoxy with improved thermal conductivity and dielectric breakdown strength [J].
Donnay, Martin ;
Tzavalas, Spiros ;
Logakis, Emmanuel .
COMPOSITES SCIENCE AND TECHNOLOGY, 2015, 110 :152-158
[10]   FAILURE MECHANISMS IN TOUGHENED EPOXY-RESINS - A REVIEW [J].
GARG, AC ;
MAI, YW .
COMPOSITES SCIENCE AND TECHNOLOGY, 1988, 31 (03) :179-223