Neutron irradiation of alloy N and 316L stainless steel in contact with a molten chloride salt

被引：13
|
作者：
Ezell, N. Dianne Bull [1 ]
Raiman, Stephen S. [1 ]
Kurley, J. Matt [1 ]
McDuffee, Joel [1 ]
机构：
[1] Oak Ridge Natl Lab, 1 Bethel Valley Rd, Oak Ridge, TN 37830 USA
来源：
NUCLEAR ENGINEERING AND TECHNOLOGY | 2021年 / 53卷 / 03期
关键词：
Corrosion; High-temperature experiment; Molten Salt Reactor; Irradiation; CORROSION; RADIOLYSIS; FLUORIDE;
D O I：
10.1016/j.net.2020.07.042
中图分类号：
TL [原子能技术]; O571 [原子核物理学];
学科分类号：
0827 ; 082701 ;
摘要：
Capsules containing NaCl-MgCl2 salt with 316L stainless steel or alloy N samples were irradiated in the Ohio State University Research Reactor for 21 nonconsecutive hours. A custom irradiation vessel was designed for this purpose, and details on its design and construction are given. Stainless steel samples that were irradiated during exposure had less corrosive attack than samples exposed to the same conditions without irradiation. Alloy N samples showed no significant effect of irradiation. This work shows a method for conducting in-reactor irradiation-corrosion experiments in static molten salts and presents preliminary data showing that neutron irradiation may decelerate corrosion of alloys in molten chloride salts.
引用
收藏
页码：920 / 926
页数：7
相关论文
共 50 条
  • [11] Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl2-MgCl2 ternary eutectic molten salt
    Liu B.
    Wei X.
    Wang W.
    Song M.
    Ding J.
    Wei, Xiaolan (xlwei@scut.edu.cn), 1600, Materials China (68): : 3202 - 3210
  • [12] Experiment and Analysis of Compatibility between New Phase Change Mixed Molten Salt and 316L Stainless Steel
    Ren, Chenxing
    Zheng, Chenghang
    Gao, Xiang
    JOURNAL OF THERMAL SCIENCE, 2024, 33 (06) : 2259 - 2273
  • [13] Corrosion resistance of 310S and 316L austenitic stainless steel in a quaternary molten salt for concentrating solar power
    Li, Xiao Long
    Wei, Xiaolan
    Lu, Jianfeng
    Ding, Jing
    Wang, Weilong
    PROCEEDINGS OF THE 9TH INTERNATIONAL CONFERENCE ON APPLIED ENERGY, 2017, 142 : 3590 - 3596
  • [14] A Comparative Study of 316L Stainless Steel and a Titanium Alloy in an Aggressive Biological Medium
    Aroussi, Djelloul
    Aour, Benaoumeur
    Bouaziz, Abdelhadi Sabik
    ENGINEERING TECHNOLOGY & APPLIED SCIENCE RESEARCH, 2019, 9 (06) : 5093 - 5098
  • [15] Barnacle cement: An etchant for stainless steel 316L?
    Sangeetha, R.
    Kumar, R.
    Doble, M.
    Venkatesan, R.
    COLLOIDS AND SURFACES B-BIOINTERFACES, 2010, 79 (02) : 524 - 530
  • [16] Effect of thermal oxidation on helium implanted 316L stainless steel
    Hong, Minsung
    Morales, Angelica Lopez
    Chan, Ho Lun
    Macdonald, Digby D.
    Balooch, Mehdi
    Xie, Yujun
    Romanovskaia, Elena
    Scully, John R.
    Kaoumi, Djamel
    Hosemann, Peter
    JOURNAL OF APPLIED PHYSICS, 2022, 132 (18)
  • [17] Nitriding of 316 stainless steel in molten fluoride salt by an electrochemical technique
    Watanabe, Takashi
    Kondo, Masatoshi
    Sagara, Akio
    ELECTROCHIMICA ACTA, 2011, 58 : 681 - 690
  • [18] Corrosion behavior of carburized 316 stainless steel in molten chloride salts
    Ren, Sen
    Chen, Yanjun
    Ye, Xiang-Xi
    Jiang, Li
    Yan, Shuai
    Liang, Jianping
    Yang, Xinmei
    Leng, Bin
    Li, Zhijun
    Chen, Zezhong
    Dai, Zhimin
    SOLAR ENERGY, 2021, 223 : 1 - 10
  • [19] Study on Corrosion Properties of Additive Manufactured 316L Stainless Steel and Alloy 625 in Seawater
    Jung, Geun-Su
    Park, Yong-Ha
    Kim, Dae-Jung
    Lim, Chae-Seon
    CORROSION SCIENCE AND TECHNOLOGY-KOREA, 2019, 18 (06): : 258 - 266
  • [20] Corrosion Behaviour of Plasma-Sprayed Nickel Coating on Type 316L Stainless Steel in High-Temperature Molten FLiNaK Salt
    Y. V. Harinath
    Ch. Jagadeeswara Rao
    S. Ningshen
    T. V. Krishna Mohan
    S. Rangarajan
    Shaju K. Albert
    Transactions of the Indian Institute of Metals, 2021, 74 : 2821 - 2833
12345