Neutron irradiation of alloy N and 316L stainless steel in contact with a molten chloride salt

被引：13
|
作者：
Ezell, N. Dianne Bull [1 ]
Raiman, Stephen S. [1 ]
Kurley, J. Matt [1 ]
McDuffee, Joel [1 ]
机构：
[1] Oak Ridge Natl Lab, 1 Bethel Valley Rd, Oak Ridge, TN 37830 USA
来源：
NUCLEAR ENGINEERING AND TECHNOLOGY | 2021年 / 53卷 / 03期
关键词：
Corrosion; High-temperature experiment; Molten Salt Reactor; Irradiation; CORROSION; RADIOLYSIS; FLUORIDE;
D O I：
10.1016/j.net.2020.07.042
中图分类号：
TL [原子能技术]; O571 [原子核物理学];
学科分类号：
0827 ; 082701 ;
摘要：
Capsules containing NaCl-MgCl2 salt with 316L stainless steel or alloy N samples were irradiated in the Ohio State University Research Reactor for 21 nonconsecutive hours. A custom irradiation vessel was designed for this purpose, and details on its design and construction are given. Stainless steel samples that were irradiated during exposure had less corrosive attack than samples exposed to the same conditions without irradiation. Alloy N samples showed no significant effect of irradiation. This work shows a method for conducting in-reactor irradiation-corrosion experiments in static molten salts and presents preliminary data showing that neutron irradiation may decelerate corrosion of alloys in molten chloride salts.
引用
收藏
页码：920 / 926
页数：7
相关论文
共 50 条
  • [1] Corrosion Behavior of Eutectic Molten Salt solution on Stainless Steel 316L
    Subari, Fuzieah
    Maksom, Hafizul Faiz
    Zawawi, Aiman
    WORLD CONFERENCE ON TECHNOLOGY, INNOVATION AND ENTREPRENEURSHIP, 2015, : 2699 - 2708
  • [2] Galvanic corrosion of Type 316L stainless steel and Graphite in molten fluoride salt
    Qiu, Jie
    Wu, Angjian
    Li, Yanhui
    Xu, Yi
    Scarlat, Raluca
    Macdonald, Digby D.
    CORROSION SCIENCE, 2020, 170 (170)
  • [3] The Corrosion Behavior of Stainless Steel 316L in Novel Quaternary Eutectic Molten Salt System
    Wang, Tao
    Mantha, Divakar
    Reddy, Ramana G.
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2017, 36 (03) : 257 - 265
  • [4] Effect of SO42- on the corrosion of 316L stainless steel in molten FLiNaK salt
    Qiu, Jie
    Leng, Bin
    Liu, Huajian
    Macdonald, Digby D.
    Wu, Angjian
    Jia, Yanyan
    Xue, Wandong
    Yu, Guojun
    Zhou, Xingtai
    CORROSION SCIENCE, 2018, 144 : 224 - 229
  • [5] Effect of CrF3 on the corrosion behaviour of Hastelloy-N and 316L stainless steel alloys in FLiNaK molten salt
    Yin, Huiqin
    Qiu, Jie
    Liu, Huajian
    Liu, Wenguan
    Wang, Yang
    Fei, Zejie
    Zhao, Sufang
    An, Xuehui
    Cheng, Jinhui
    Chen, Tao
    Zhang, Peng
    Yu, Guojun
    Xie, Leidong
    CORROSION SCIENCE, 2018, 131 : 355 - 364
  • [6] CORROSION OF 316L STAINLESS STEEL ALLOY AND HASTELLOY-N SUPERALLOY IN MOLTEN EUTECTIC LiF-NaF-KF SALT AND INTERACTION WITH GRAPHITE
    Sellers, Robert S.
    Cheng, Wei-Jen
    Kelleher, Brian C.
    Anderson, Mark H.
    Sridharan, Kumar
    Wang, Chaur-Jeng
    Allen, Todd R.
    NUCLEAR TECHNOLOGY, 2014, 188 (02) : 192 - 199
  • [7] Corrosion Mechanism and Properties of 316L Stainless Steel in NaCl-KCl Molten Salt at High Temperatures
    Lv, Ruimin
    Tang, Xian
    Ying, Zhemian
    Ai, Hua
    Sun, Hua
    Zhang, Wei
    Wang, Ying
    Cheng, Jinjuan
    Yan, Long
    CRYSTALS, 2025, 15 (03)
  • [8] Preliminary investigation on the effect of irradiation on tribocorrosion behavior of 316L stainless steel alloy
    Farid, Osama M.
    Moamen, O. A. Abdel
    Shehata, M. M.
    JOURNAL OF RADIATION RESEARCH AND APPLIED SCIENCES, 2019, 12 (01) : 367 - 374
  • [9] Electrochemical study of the dissolution of oxide films grown on type 316L stainless steel in molten fluoride salt
    Qiu, Jie
    Macdonald, Digby D.
    Schoell, Ryan
    Han, Junsoo
    Mastromarino, Sara
    Scully, John R.
    Kaoumi, Djamel
    Hosemann, Peter
    CORROSION SCIENCE, 2021, 186
  • [10] Electrochemical corrosion behavior of 316L stainless steel in molten fluorides with a temperature gradient
    Wang, Yanli
    Wu, Jiajie
    Wang, Changxuan
    Zhang, Shenghua
    ELECTROCHEMISTRY COMMUNICATIONS, 2019, 109
12345