Development of a platinum-enhanced radiopaque stainless steel (PERSS®)7

被引：5

作者：

Craig, CH ^{[1
]}

Radisch, HR ^{[1
]}

Trozera, TA ^{[1
]}

Turner, PC ^{[1
]}

Govier, RD ^{[1
]}

Vesely, EJ ^{[1
]}

Gokcen, NA ^{[1
]}

Friend, CM ^{[1
]}

Edwards, MR ^{[1
]}

机构：

[1] Boston Sci Corp Intervent Technol, R&D, San Diego, CA 92123 USA

来源：

STAINLESS STEELS FOR MEDICAL AND SURGICAL APPLICATIONS | 2003年 / 1438卷

关键词：

stainless steel; platinum; coronary stent; radiopacity; New PHACOMP;

D O I：

10.1520/STP11151S

中图分类号：

TH7 [仪器、仪表];

学科分类号：

0804 ; 080401 ; 081102 ;

摘要：

Balloon-expandable coronary stents may be made of stainless steel conforming to ASTM or ISO specifications, referred to by ASTM as UNS S31673 alloys. A need exists for an alloy with enhanced radiopacity to make stents more visible radiographically and more effective clinically. A research program was initiated with the objectives of enhancing fluoroscopic radiopacity while maintaining adherence to the ASTM and ISO specifications. These objectives were ultimately achieved by adding a noble metal, platinum, to UNS S31673 by vacuum induction melting a commercially-available alloy. Freedom of the resulting microstructure from formation of harmful topologically close packed phases was ensured by use of phase computation methodology (New PHACOMP), and confirmed by X-ray diffraction and transmission electron microscopy. Platinum was chosen since it is over twice as dense as nickel and, with approximately half its effect as an austenitizer, allows nickel content to be reduced to a minimum level.

引用

页码：28 / 38

页数：11

共 17 条

[1] [Anonymous], 1964, METAL PROGR
[2] *ASM INT, 1989, ASM HDBR, V17, P323
[3] BEDDOES J, 1999, INTRO STAINLESS STEE, P137
[4] COVINO BS, 2003, ASTM STP, V1438
[5] A combined solubility product new PHACOMP approach for estimating temperatures of secondary solidification reactions in superalloy weld metals containing Nb and C
DuPont, JN
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (05): : 1449 - 1456
[6] Hubbell J.H., 1997, Tables of X-ray mass attenuation coefficients and mass energy-absorption coefficients (version 1.03), DOI DOI 10.18434/T4D01F
[7] McGill IR, 1990, PLATIN MET REV, V34, P144
[8] Mcgill I. R., 1990, PLATIN MET REV, V34, P85
[9] MOEMA J, 2001, INFLUENCE GOLD RUTHE
[10] MONNARZ P, 1911, METALLURGIE, V8, P160

← 1 2 →