Comparison of magnetic properties of austenitic stainless steel after ion irradiation

被引：3
作者：
Xu, Chaoliang [1 ]
Liu, Xiangbing [1 ]
Xue, Fei [1 ]
Li, Yuanfei [1 ]
Qian, Wangjie [1 ]
机构：
[1] Suzhou Nucl Power Res Inst, Suzhou 215004, Jiangsu, Peoples R China
来源：
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS | 2018年 / 427卷
基金：
中国国家自然科学基金;
关键词：
Austenitic stainless steel; Irradiation; Magnetization; Martensite; Coercivity; MARTENSITIC-TRANSFORMATION; TEMPERATURE; XE; IMPLANTATION; CRACKING; REACTOR; ALLOYS; SENSOR; IASCC; IRON;
D O I：
10.1016/j.nimb.2018.04.041
中图分类号：
TH7 [仪器、仪表];
学科分类号：
0804 ; 080401 ; 081102 ;
摘要：
Specimens of austenitic stainless steel (ASS) were irradiated with H, Fe and Xe ions at room temperature. The vibrating sample magnetometer (VSM) and grazing incidence X-ray diffraction (GIXRD) were used to analyze the magnetic properties and martensite formation. The magnetic hysteresis loops indicated that higher irradiation damage causes more significant magnetization phenomenon. Under the same damage level, Xe irradiation causes the most significant magnetization, Fe irradiation is the second, and H irradiation is the least. A similar martensite amount variation with irradiation can be obtained. The coercivity H-c increases first to 2 dpa and then decreases continuously with irradiation damage for Xe irradiation. At the same damage lever, H irradiation causes a largest H-c and Xe irradiation causes a minimal one.
引用
收藏
页码：87 / 90
页数：4
相关论文
共 50 条
  • [31] Effects of Si on Stress Corrosion Cracking Properties of Austenitic Stainless Steel
    Weijia, Gong
    Shuai, Chen
    Lupeng, Liu
    Donghai, Du
    RARE METAL MATERIALS AND ENGINEERING, 2025, 54 (01) : 109 - 117
  • [32] Effect of ultrafine grain refinement on hydrogen embrittlement of metastable austenitic stainless steel
    Mine, Yoji
    Horita, Nobuaki
    Horita, Zenji
    Takashima, Kazuki
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2017, 42 (22) : 15415 - 15425
  • [33] Microstructural Heterogeneity and Mechanical Properties of a Welded Joint of an Austenitic Stainless Steel
    Munoz, Jairo Alberto
    Dolgach, Egor
    Tartalini, Vanina
    Risso, Pablo
    Avalos, Martina
    Bolmaro, Raul
    Cabrera, Jose Maria
    METALS, 2023, 13 (02)
  • [34] SURFACE MODIFICATION OF AUSTENITIC STAINLESS-STEEL BY TITANIUM ION-IMPLANTATION
    EVANS, PJ
    HYVARINEN, J
    SAMANDI, M
    SURFACE & COATINGS TECHNOLOGY, 1995, 71 (02) : 151 - 158
  • [35] Diffusion profiles after nitrocarburizing austenitic stainless steel
    Wu, D.
    Ge, Y.
    Kahn, H.
    Ernst, F.
    Heuer, A. H.
    SURFACE & COATINGS TECHNOLOGY, 2015, 279 : 180 - 185
  • [36] A COMPARISON OF RADIATION SHIELDING OF STAINLESS STEEL WITH DIFFERENT MAGNETIC PROPERTIES
    Calik, Adnan
    Akbunar, Sahin
    Ucar, Nazim
    Yilmaz, Nihat
    Karakas, Mustafa Serdar
    Akkurt, Iskender
    NUCLEAR TECHNOLOGY & RADIATION PROTECTION, 2014, 29 (03) : 186 - 189
  • [37] Magnetic Properties of Single Crystalline Expanded Austenite Obtained by Plasma Nitriding of Austenitic Stainless Steel Single Crystals
    Menendez, Enric
    Templier, Claude
    Garcia-Ramirez, Pablo
    Santiso, Jose
    Vantomme, Andre
    Temst, Kristiaan
    Nogues, Josep
    ACS APPLIED MATERIALS & INTERFACES, 2013, 5 (20) : 10118 - 10126
  • [38] Magnetic properties and microstructural characterization of cold-rolled and annealed 317L austenitic stainless steel
    Sandim, M. J. R.
    Mauro, V
    Tavares, S. S. M.
    Zilnyk, K. D.
    Sandim, H. R. Z.
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2021, 539
  • [39] The influence of ion energy on the nitriding behavior of austenitic stainless steel
    Leigh, S
    Samandi, M
    Collins, GA
    Short, KT
    Martin, P
    Wielunski, L
    SURFACE & COATINGS TECHNOLOGY, 1996, 85 (1-2) : 37 - 43
  • [40] Comparison of Nitriding Behavior for Austenitic Stainless Steel 316Ti and Super Austenitic Stainless Steel 904L
    Maendl, Stephan
    Manova, Darina
    METALS, 2024, 14 (06)
12345