Characterization of as-deposited and annealed Cr-C alloy coatings produced from a trivalent chromium bath

被引：69
|
作者：
Ghaziof, S. [1 ]
Golozar, M. A. [1 ]
Raeissi, K. [1 ]
机构：
[1] Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran
来源：
JOURNAL OF ALLOYS AND COMPOUNDS | 2010年 / 496卷 / 1-2期
关键词：
Cr-C alloy; Coating; Amorphous; Nanocrystalline; Annealing; Corrosion resistance; ELECTROCHEMICAL-BEHAVIOR; MECHANICAL-PROPERTIES; FORMIC-ACID; ELECTRODEPOSITION; LAYER;
D O I：
10.1016/j.jallcom.2010.02.101
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Amorphous Cr-C alloy coatings were electrodeposited from a trivalent chromium bath containing formic acid. The effects of plating parameters such as pH and current density on composition, structure, morphology and corrosion behaviour of as-deposited coatings were investigated. Results showed that the suitable current density for Cr-C alloy electrodeposition is increased as the pH is decreased. Furthermore, by decreasing the pH, higher amount of carbon was introduced into the coatings. The Cr-C alloy coatings deposited at lower pH showed higher passive current density on Tafel plot. By annealing the amorphous Cr-C alloy coatings at 300 degrees C. a nanocrystalline structure having higher hardness was obtained. However, the corrosion resistance was seen to be impaired. Annealing at 600 degrees C led to the precipitation of Cr23C6 which resulted in a higher hardness. The formation of Cr23C6 enhanced the corrosion resistance of coatings due to an increase in corrosion potential. However, formation of micro-cells between the Cr23C6 precipitates and bulk chromium prevented the passive film formation. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码：164 / 168
页数：5
相关论文
共 50 条
  • [21] A Comparison of the Corrosion Resistance and Wear Resistance Behavior of Cr-C, Ni-P and Ni-B Coatings Electroplated on 4140 Alloy Steel
    Sheu, Hung-Hua
    Syu, Jian-Huang
    Liu, Yih-Ming
    Hou, Kung-Hsu
    Ger, Ming-Der
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2018, 13 (04): : 3267 - 3278
  • [22] Electrodeposition of corrosion-resistant Cr–P and Cr–P–W coatings from solutions based on compounds of trivalent chromium
    V. V. Kuznetsov
    E. G. Vinokurov
    A. V. Telezhkina
    E. A. Filatova
    Journal of Solid State Electrochemistry, 2019, 23 : 2367 - 2376
  • [23] Establishing relationships between bath chemistry, electrodeposition and microstructure of Co-W alloy coatings produced from a gluconate bath
    Weston, D. P.
    Harris, S. J.
    Shipway, P. H.
    Weston, N. J.
    Yap, G. N.
    ELECTROCHIMICA ACTA, 2010, 55 (20) : 5695 - 5708
  • [24] Preparation and characterisation of electrodeposited Ni-Cr/Al2O3 nanocomposite coatings from a trivalent chromium-based bath
    Khosroshahi, R. A.
    Manesh, M. R. Kiyan
    Parvini, N.
    INTERNATIONAL JOURNAL OF SURFACE SCIENCE AND ENGINEERING, 2012, 6 (1-2) : 92 - 100
  • [25] Estimation of the protective ability of chromium coatings deposited from sulfate and methanesulfonate electrolytes based on Cr(III)
    Danilov, F. I.
    Protsenko, V. S.
    Kityk, A. A.
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2014, 50 (05) : 672 - 678
  • [26] Electrodeposition and characterization of Fe-Cr-P amorphous alloys from trivalent chromium sulfate electrolyte
    Li, Baosong
    Lin, An
    Wu, Xu
    Zhang, Yeming
    Gan, Fuxing
    JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 453 (1-2) : 93 - 101
  • [27] Characteristics and corrosion behavior of as-deposited and heat-treated Co-Cr/ZrO2 coatings electrodeposited from Cr(III) baths
    Mahmoudi, E.
    Mohitfar, S. H.
    Mahdavi, S.
    MATERIALS CHEMISTRY AND PHYSICS, 2021, 272
  • [28] Wear and corrosion of Co-Cr coatings electrodeposited from a trivalent chromium solution: Effect of heat treatment temperature
    Mardanifar, Ali
    Mohseni, Ali
    Mahdavi, Soheil
    SURFACE & COATINGS TECHNOLOGY, 2021, 422
  • [29] A chrome coating from a trivalent chromium bath containing extremely low concentration of Cr3+ ions
    Katirci, Ramazan
    INTERNATIONAL JOURNAL OF SURFACE SCIENCE AND ENGINEERING, 2016, 10 (01) : 73 - 85
  • [30] MULTI-RESPONSE OPTIMISATION OF ELECTRODEPOSITION OF NANO-CRYSTALLINE COMPOSITE COATINGS Cr-Cr3P IN STATU NASCENDI FROM TRIVALENT CHROMIUM-BATHS
    Vinokurov, E. G.
    Burukhina, T. F.
    Napedenina, E. Yu
    IZVESTIYA VYSSHIKH UCHEBNYKH ZAVEDENII KHIMIYA I KHIMICHESKAYA TEKHNOLOGIYA, 2021, 64 (03): : 73 - 81
12345