New amorphous and nanocrystalline alloys based on the Ni-Si-B system

The glass formation and crystallization of a Ni36Fe32Ta7Si8B17 alloy is reported. In its equilibrium state it has a complex constitution made of at least four phases. It starts melting at 1227 K and displays a liquidus at 1460 K, but it shows a tendency to undercool even on cooling at 10 K/min in a HTDSC cell. Amorphous ribbons were produced by melt spinning. In DSC experiments the crystallization of the amorphous alloy occurs with a primary reaction giving a peak skewed on the high temperature side with onset at 836 K using an heating rate of 40 K/min. XRD analysis and TEM observations demonstrate that crystals with size below 10 nm and lattice parameter close to that of Ni are formed during this transformation. The mechanism of crystallization is very sensitive to changes in composition. In fact, nanocrystals are not found in alloys easily amorphized as the present one but containing a different ratio of metallic elements.