Fabrication of Al5083 surface composites reinforced by CNTs and cerium oxide nano particles via friction stir processing

In the present investigation, friction stir processing (FSP) was utilized to incorporate Multi Walled Carbon Nano Tubes (MWCNT) and nanosized cerium oxide particles into the matrix of Al5083 alloy to form surface reinforced composites. The effect of these nanosized reinforcements either separately or in the combined form, on microstructural modification, mechanical properties and corrosion resistance of FSPed Al5083 surface composites was studied. A threaded cylindrical hardened steel tool was used with the rotation speeds of 600 and 800 rpm and travel speeds of 35 and 45 mm/min and a tilt angle of 5 degrees. Mechanical properties and corrosion resistance of FSPed samples were evaluated and compared with the base alloy. The maximum tensile strength and hardness value were achieved for the hybrid composite containing a mixture of CNTs and cerium oxide in the volume ratio of 75-25, respectively, whereas a significant increase in pitting resistance of the base alloy was obtained when cerium oxide alone was incorporated. The corrosion behavior of the samples was investigated by potentiodynamic polarization tests and assessed in term of pitting potential and passivation range. Microstructural analysis carried out by using optical and electron microscopes showed that reinforcements are well dispersed inside the nugget zone (NZ), and remarkable grain refinement is gained. The study was aimed to fabricate surface composites with improved mechanical properties and corrosion resistance simultaneously. (C) 2014 Elsevier B.V. All rights reserved.