Corrosion and pitting of 6060 series aluminium after 2 years exposure in seawater splash, tidal and immersion zones

被引：77

作者：

Liang, Mengxia ^{[1
]}

Melchers, Robert ^{[1
]}

Chaves, Igor ^{[1
]}

机构：

[1] Univ Newcastle, Ctr Infrastruct Performance & Reliabil, Callaghan, NSW 2308, Australia

来源：

CORROSION SCIENCE | 2018年 / 140卷

基金：

澳大利亚研究理事会;

关键词：

Aluminium; Alloy; Pitting corrosion; Intergranular corrosion; INTERGRANULAR CORROSION; COPPER CONTENT; PASSIVITY BREAKDOWN; PIT INITIATION; MILD-STEEL; BEHAVIOR; ALLOY; PROBABILITY; TRANSITION; COASTAL;

D O I：

10.1016/j.corsci.2018.05.036

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

New longer-term observations of corrosion and pitting of 6060-grade aluminium alloy showed that the most intensive pitting and corrosion occurred in the marine immersion zone. After 2 years exposure the corrosion morphology included shallow and deep pits, intergranular corrosion and crystallographic attack. The deepest pits showed complex morphologies, spatially and with depth. This is considered the result of localized anoxic conditions formed under accumulated corrosion products. Less severe corrosion was observed in the splash and tidal zones. For these the pit morphologies were less complex.

引用

页码：286 / 296

页数：11

共 55 条

[1] Localized alkaline corrosion of alloy AA5083 in neutral 3.5% NaCl solution [J].

Aballe, A ;

Bethencourt, M ;

Botana, FJ ;

Cano, MJ ;

Marcos, M .

CORROSION SCIENCE, 2001, 43 (09) :1657-1674

[2] Effects of solar radiation on growth, photosynthesis and respiration of marine macroalgae from the Arctic [J].

Aguilera, J ;

Karsten, U ;

Lippert, H ;

Vögele, B ;

Philipp, E ;

Hanelt, D ;

Wiencke, C .

MARINE ECOLOGY PROGRESS SERIES, 1999, 191 :109-119

[3]

Ahmad Z., 2011, Recent Trends in Processing and Degradation of Aluminium Alloys

[4] Toxicity of Al to Desulfovibrio desulfuricans [J].

Amonette, JE ;

Russell, CK ;

Carosino, KA ;

Robinson, NL ;

Ho, JT .

APPLIED AND ENVIRONMENTAL MICROBIOLOGY, 2003, 69 (07) :4057-4066

[5]

[Anonymous], CORROS PREV

[6]

[Anonymous], G13 ASTM

[7]

[Anonymous], 2007, CORROSION BEHAVIOUR

[8]

[Anonymous], 4 INT C REC TRENDS S

[9]

[Anonymous], 2014, CORROS PREVENT CONTR

[10]

[Anonymous], 1974, ASTM STP

← 1 2 3 4 5 6 →