Effect of welding parameters on microstructure and mechanical properties of friction stir welded joints of a super high strength Al-Zn-Mg-Cu aluminum alloy

被引：80

作者：

Zhang, Fei ^{[1
]}

Su, Xuekuan ^{[1
]}

Chen, Ziyong ^{[1
]}

Nie, Zuoren ^{[1
]}

机构：

[1] Beijing Univ Technol, Coll Mat Sci & Engn, Beijing 100124, Peoples R China

来源：

MATERIALS & DESIGN | 2015年 / 67卷

关键词：

Super high strength aluminum alloy; Friction stir welding; Microstructure; Mechanical properties; EVOLUTION; ZONE; ER;

D O I：

10.1016/j.matdes.2014.10.055

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Samples made of a super high strength aluminum alloy with high Zn content were friction stir welded with rotation rates of 350-950 rpm and welding speeds of 50-150 mm/min. The effect of welding parameters on the microstructure and mechanical properties was investigated. It was observed that the grain size of the nugget zones decreased with the increasing welding speed or the decreasing tool rotation rate. Most of the strengthening precipitates in the nugget zone were dissolved back and the intragranular and grain boundary precipitates in the heat affected zone coarsened significantly. The greatest ultimate tensile strength of 484 MPa and largest elongation of 9.4 were obtained at 350 rpm -100 mm/min and 350 rpm -50 mm/min, respectively. The ultimate tensile strength and elongation deteriorated drastically when rotation rate increased from 350 to 950 rpm at a constant welding speed of 100 mm/min. (C) 2014 Elsevier Ltd. All rights reserved.

引用

页码：483 / 491

页数：9

共 37 条

[1]

[Anonymous], 2002, GBT 228 2002 ISO6892

[2] Tensile properties of friction stir welded joints of 2024 aluminum alloys in different heat-treated-state [J].

Aydin, Hakan ;

Bayram, Ali ;

Uguz, Agah ;

Akay, Kemal Sertan .

MATERIALS & DESIGN, 2009, 30 (06) :2211-2221

[3]

Bird CR, 2004, PROCEEDINGS OF THE F

[4]

Cao X, 2007, FRICTION STIR WELDING AND PROCESSING IV, P213

[5]

Cao X, 2007, P 3 INT C LIGHT MET, P158

[6] The investigation of typical welding defects for 5456 aluminum alloy friction stir welds [J].

Chen, Hua-Bin ;

Yan, Keng ;

Lin, Tao ;

Chen, Shan-Ben ;

Jiang, Cheng-Yu ;

Zhao, Yong .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 433 (1-2) :64-69

[7] Microstructure mapping in friction stir welds of 7449 aluminium alloy using SAXS [J].

Dumont, M. ;

Steuwer, A. ;

Deschamps, A. ;

Peel, M. ;

Withers, P. J. .

ACTA MATERIALIA, 2006, 54 (18) :4793-4801

[8] Advanced high-strength aluminum-base materials [J].

Fridlyander, IN ;

Dobromyslov, AV ;

Tkachenko, EA ;

Senatorova, OG .

METAL SCIENCE AND HEAT TREATMENT, 2005, 47 (7-8) :269-275

[9] Evolution of microstructure and mechanical properties in naturally aged 7050 and 7075 Al friction stir welds [J].

Fuller, Christian B. ;

Mahoney, Murray W. ;

Calabrese, Mike ;

Micona, Leanna .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (09) :2233-2240

[10] Effect of welding parameters on microstructure and mechanical properties of friction stir welded Al-Mg-Er alloy [J].

Hao, H. L. ;

Ni, D. R. ;

Huang, H. ;

Wang, D. ;

Xiao, B. L. ;

Nie, Z. R. ;

Ma, Z. Y. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 559 :889-896

← 1 2 3 4 →