Defect states of ZnO nanoparticles: Discrimination by time-resolved photoluminescence spectroscopy

被引：112

作者：

Han, Noh Soo ^{[1
]}

Shim, Hyeong Seop ^{[1
]}

Seo, Joo Hee ^{[1
]}

Kim, Sun Young ^{[1
]}

Park, Seung Min ^{[1
]}

Song, Jae Kyu ^{[1
]}

机构：

[1] Kyung Hee Univ, Dept Chem, Seoul 130701, South Korea

来源：

JOURNAL OF APPLIED PHYSICS | 2010年 / 107卷 / 08期

关键词：

HEXAGONAL CONE; ROD SHAPES; EMISSION; CATHODOLUMINESCENCE; FILMS; UV;

D O I：

10.1063/1.3382915

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

ZnO nanoparticles with different shapes and sizes were prepared by changing coordinating ligands. Hexagonal cones presented UV and green (similar to 500 nm) emissions, which originated from excitons and defects, respectively. Oxygen vacancies were found to be major defects in the hexagonal cones. Blue emission at similar to 440 nm was observed for hexagonal plates, and analyses of time-resolved photoluminescence spectra showed that two transitions were responsible for this blue emission, because transitions from Zn-i to the valence band (430 nm) and from Zn-i to V-Zn (480 nm) were distinguished by emission wavelengths and lifetimes. The visible emissions from defects were related to the roles of coordinating ligands. (C) 2010 American Institute of Physics. [doi:10.1063/1.3382915]

引用

页数：7

共 35 条

[31] Optical detection of electron paramagnetic resonance in room-temperature electron-irradiated ZnO [J].

Vlasenko, LS ;

Watkins, GD .

PHYSICAL REVIEW B, 2005, 71 (12)

[32] Highly polarized photoluminescence and photodetection from single indium phosphide nanowires [J].

Wang, JF ;

Gudiksen, MS ;

Duan, XF ;

Cui, Y ;

Lieber, CM .

SCIENCE, 2001, 293 (5534) :1455-1457

[33] Correlations between surface-excitonic emission bands in ZnO nanowires [J].

Wischmeier, L. ;

Voss, T. ;

Rueckmann, I. ;

Gutowski, J. .

NANOTECHNOLOGY, 2008, 19 (13)

[34] Photoluminescence and cathodoluminescence studies of stoichiometric and oxygen-deficient ZnO films [J].

Wu, XL ;

Siu, GG ;

Fu, CL ;

Ong, HC .

APPLIED PHYSICS LETTERS, 2001, 78 (16) :2285-2287

[35] Strong localization effect in temperature dependence of violet-blue emission from ZnO nanoshells [J].

Zeng, Haibo ;

Li, Zhigang ;

Cai, Weiping ;

Liu, Peisheng .

JOURNAL OF APPLIED PHYSICS, 2007, 102 (10)

← 1 2 3 4 →