Corrosion Behaviour of T92 Steel in NaCl Solution

被引：9

作者：

Long, Yi ^{[1
,2
]}

Feng, Chao ^{[1
,2
]}

Peng, Bicao ^{[1
,2
]}

Xie, Yi ^{[1
,2
]}

Wang, Jun ^{[1
,2
]}

Zhang, Minghua ^{[3
]}

Wu, Yuanhui ^{[4
]}

Wu, Tangqing ^{[3
]}

Yin, Fucheng ^{[3
]}

机构：

[1] State Grid Hunan Elect Power Co, Elect Power Res Inst, Changsha 410007, Hunan, Peoples R China

[2] Hunan Xiangdian Boiler & Pressure Vessel Inspect, Changsha 410001, Hunan, Peoples R China

[3] Xiangtan Univ, Key Lab Mat Design & Preparat Technol Hunan Prov, Xiangtan 411105, Peoples R China

[4] Zunyi Normal Coll, Sch Chem & Chem Engn, Zunyi 563002, Peoples R China

来源：

INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE | 2017年 / 12卷 / 06期

基金：

中国国家自然科学基金;

关键词：

T92; salt spray test; electrochemical impedance spectroscopy (EIS); scanning electron microscope (SEM); pitting; HIGH STRENGTH STEEL; CRACKING BEHAVIOR; STRESS; OXIDATION; HYDROGEN; ALLOYS;

D O I：

10.20964/2017.06.13

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

In the paper, the effects of NaCl on the corrosion behaviour of T92 steel at room temperature were studied by neutral salt spray test, electrochemical technology and scanning electron microscope. The results show that the corrosion rate of T92 steel continuously increase with the NaCl concentration during the neutral salt spray tests. NaCl promotes the anodic process rather than the cathodic process of the T92 steel in solution. In NaCl solutions with low concentrations, T92 steel undergoes uniform corrosion, wheres its corrosion behaviour will develop into pitting as the concentration of NaCl increase. The formation and development mechanism for the corrosion pitting are also discussed in the paper.

引用

页码：5104 / 5120

页数：17

共 50 条

[31] Microstructure and Mechanical Properties of Heat-treated T92 Martensitic Heat Resistant Steel
Kannan, P. Rajesh
Muthupandi, V.
Arivazhagan, B.
Devakumaran, K.
HIGH TEMPERATURE MATERIALS AND PROCESSES, 2017, 36 (08) : 771 - 778
[32] Effects of Tempering Temperature on the Microstructure and Mechanical Properties of T92 Heat-Resistant Steel
Zhao, Dandan
Zhang, Shenghua
Zhang, Hai
Li, Shilei
Xiao, Huifang
Wang, Yanli
Wang, Xitao
METALS, 2019, 9 (02)
[33] Effect of Pre-Oxidation on the Steam Oxidation of Heat-Resistant Steel T92
Xu Hong
Liang Zhiyuan
Ding Jianliang
Zhao Qinxin
Guan Shipian
HIGH TEMPERATURE MATERIALS AND PROCESSES, 2018, 37 (08) : 733 - 739
[34] Microstructure evolution and life assessment of T92 steel during long-term creep
Nie, M.
Zhang, J.
Huang, F.
Liu, J. W.
Zhu, X. K.
Chen, Z. L.
Ouyang, L. Z.
JOURNAL OF ALLOYS AND COMPOUNDS, 2014, 588 : 348 - 356
[35] Comparative Study on High Temperature Oxidation of T92 Steel in Dry and Wet Oxyfuel Environments
K. Chandra
A. Kranzmann
R. Saliwan Neumann
F. Rizzo
Oxidation of Metals, 2015, 84 : 463 - 490
[36] Influence of Cement Superplasticizer on Steel Corrosion in 3.5 % NaCl Solution
Tammam, Reham H.
Mogoda, A. S.
Gharbawy, Mohamed H.
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2020, 15 (09): : 8408 - 8421
[37] Corrosion degradation of chromium coatings on steel in NaCl concentrated solution
I. V. Petukhov
M. G. Shcherban’
V. I. Kichigin
A. V. Zaitseva
E. V. Mikhailov
S. V. Zavodchikov
Protection of Metals, 2006, 42 : 378 - 388
[38] Corrosion degradation of chromium coatings on steel in NaCl concentrated solution
Petukhov, I. V.
Shcherban, M. G.
Kichigin, V. I.
Zaitseva, A. V.
Mikhailov, E. V.
Zavodchikov, S. V.
PROTECTION OF METALS, 2006, 42 (04): : 378 - 388
[39] EFFECT OF GALVANIZING ON THE CORROSION OF STEEL IN CONCRETE IMMERSED IN NACL SOLUTION
HILDEBRAND, H
SCHWENK, W
WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1986, 37 (04): : 163 - 169
[40] Effects of crevice geometry on corrosion behavior of steel in NaCl solution
Tada, Eiji
Maeda, Hatsumi
Ooi, Azusa
Nishikata, Atsushi
Zairyo to Kankyo/ Corrosion Engineering, 2021, 70 (01): : 10 - 17

← 1 2 3 4 5 →