Oxidation properties of Zr-Nb alloys at 500-600°C under low oxygen potentials

被引：31

作者：

Arima, T ^{[1
]}

Miyata, K ^{[1
]}

Inagaki, Y ^{[1
]}

Idemitsu, K ^{[1
]}

机构：

[1] Kyushu Univ, Fac Engn, Inst Environm Syst, Fukuoka 8128581, Japan

来源：

CORROSION SCIENCE | 2005年 / 47卷 / 02期

关键词：

Zr-Nb alloy; oxidation; XRD; EPMA;

D O I：

10.1016/j.corsci.2004.06.011

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Zr-Nb alloys with 1-10 wt.% Nb content were oxidized at 500-600degreesC in the CO-CO2 gas mixtures. The oxidation weight gain increased with Nb content and the kinetics except for Zr-1Nb alloy changed from cubic rate to linear one at 600degreesC for a long period of time, 7d. The cubic rate constant was almost insensitive to oxygen potential of oxidizing atmosphere. As the oxidation resistance deteriorated, the volume ratio of tetragonal to monoclinic zirconia phase and the relevant compressive stress in oxide film decreased with increase of Nb content. Before and after oxidation, Nb re-distribution could not be observed under the present experimental condition. (C) 2004 Elsevier Ltd. All rights reserved.

引用

页码：435 / 446

页数：12

共 39 条

[1]

Abriata J.P., 1982, B ALLOY PHASE DIAGRA, V3, P1

[2] The oxidation kinetics and the structure of the oxide film on Zircaloy before and after the kinetic transition [J].

Arima, T ;

Masuzumi, T ;

Furuya, H ;

Idemitsu, K ;

Inagaki, Y .

JOURNAL OF NUCLEAR MATERIALS, 2001, 294 (1-2) :148-153

[3] Oxidation kinetics of Zircaloy-2 between 450°C and 600°C in oxidizing atmosphere [J].

Arima, T ;

Moriyama, K ;

Gaja, N ;

Furuya, H ;

Idemitsu, K ;

Inagaki, Y .

JOURNAL OF NUCLEAR MATERIALS, 1998, 257 (01) :67-77

[4] ZIRCONIA POWDERS AND ZIRCALOY OXIDE-FILMS - TETRAGONAL PHASE EVOLUTION DURING 400-DEGREES-C AUTOCLAVE TESTS [J].

BARBERIS, P .

JOURNAL OF NUCLEAR MATERIALS, 1995, 226 (1-2) :34-43

[5]

BEIE HJ, 1994, AM SOC TEST MATER, V1245, P615, DOI 10.1520/STP15212S

[6]

Charquet D., 1987, ZIRCONIUM NUCL IND, P431

[7] OXIDATION AND HYDROGEN UPTAKE OF ZR BASED NB ALLOYS AT 400-DEGREES-C UNDER 10 MPA H2O STEAM ATMOSPHERE [J].

CHOO, KN ;

PYUN, SI ;

KIM, YS .

JOURNAL OF NUCLEAR MATERIALS, 1995, 226 (1-2) :9-14

[8] KINETICS AND MECHANISM OF OXIDATION OF ZIRCALOY-2 AT 350-500 DEGREES C [J].

DAWSON, JK ;

LONG, G ;

SEDDON, WE ;

WHITE, JF .

JOURNAL OF NUCLEAR MATERIALS, 1968, 25 (02) :179-&

[9]

Etoh Y., 1996, ASTM STP, V1295, P825

[10]

Eucken C.M., 1989, ASTM STP, P113

← 1 2 3 4 →