Heavy-ion irradiation dependence of the superconducting properties of (Cu,C)Ba2Ca3Cu4O10.5-δ

To enhance or improve critical currents density (J(c)) and irreversibility field (H-irr) of (Cu,C)Ba2Ca3Cu4O10.5-delta ((Cu,C)-1234), pinning centers were introduced by heavy-ion irradiation. The polycrystalline samples were irradiated with An(15+) ions (240 MeV energy) at various fluence of 1 x 10(11), 2.5 x 10(11) and 5 x 10(11) ions/cm(2). J(c) and H-irr were determined for the irradiated samples as well as unirradiated samples. J(c) (77 K, 1 T) increase from 3.9 x 10(4) A/cm(2) to 4.1 x 10(6) A/cm(2) for at fluence of 1 x 10(11) ions/cm(2) of heavy-ion irradiated sample and decreases with further increase of fluence. These results indicate the possibility of further enhancement of Jc and of achieving a very high H-irr of (Cu,C)-1234 below a fluence of 1 x 10(11) ions/cm(2). (C) 2003 Elsevier Science B.V. All rights reserved.