Study on fatigue failure mechanism at various temperatures of a high-speed railway wheel steel

被引：15

作者：

Fang, Xiu-Yang ^{[1
]}

Zhao, Yong-Xiang ^{[1
]}

Liu, Huan-Wei ^{[2
]}

机构：

[1] Southwest Jiaotong Univ, Sch Mech Engn, Chengdu 610031, Sichuan, Peoples R China

[2] Southwest Jiaotong Univ, State Key Lab Tract Power, Chengdu 610031, Sichuan, Peoples R China

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2017年 / 696卷

关键词：

Railway wheel steel; Fatigue; Failure mechanism; Microstructure; Temperature; PEARLITE;

D O I：

10.1016/j.msea.2017.04.042

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The fatigue life and limit of the wheel rim and the wheel web position of a high-speed railway wheel steel at various testing temperatures (60 to 60 degrees C) were investigated. Both microstructures and fracture morphologies were observed in details. The fatigue failure mechanism at various temperatures was discussed. The results demonstrated that the wheel rim had a longer fatigue lifetime and a higher value of fatigue limit than the corresponding properties of the wheel web due to various microstructural distributions. The temperature, microstructure and stress amplitude had a significant impact on the fatigue initiation and propagation. The typical features including the propagation zone of regular fan-like shapes, the fatigue step, the gray wear facets and the fatigue striation were observed on the fracture surface, which were related to the failure mechanism transition.

引用

页码：299 / 314

页数：16

共 50 条

[31] High-speed tensile tests on high-manganese steel at low temperatures [J].

Dieffenbach, Tonja ;

Treutler, Kai ;

Wesling, Volker .

MATERIALS TESTING, 2023, 65 (01) :124-133

[32] Influence of Service Temperatures on the Fatigue Behaviour of Railway Wheel and Tyre Steels [J].

Peters, Carsten J. ;

Eifler, Dietmar .

MATERIALS TESTING, 2009, 51 (11-12) :748-754

[33] A Study of the Carbides in High-Speed Steel Rolls [J].

Luan Yikun ;

Song Nannan ;

Kang Xiuhong ;

Li Dianzhong .

THERMEC 2009, PTS 1-4, 2010, 638-642 :3356-3361

[34] Effect of cerium on the cleanliness of spring steel used in fastener of high-speed railway [J].

Liu Yanqiang ;

Wang Lijun ;

Chou Kuochih .

JOURNAL OF RARE EARTHS, 2014, 32 (08) :759-766

[35] A study of casting high-boron high-speed steel roll materials [J].

Li, X. ;

Hou, J. ;

Qu, Y. ;

Fu, H. .

MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2015, 46 (10) :1029-1038

[36] Study on Mechanism and Influencing Factors of Wheel Strengthening and Toughening of High-Speed and Heavy-Load Train [J].

Jia, Tuosheng ;

Shen, Zhigang ;

Liu, Cuirong ;

Zhao, Xinglong ;

Zhang, Xiaofeng .

CRYSTALS, 2023, 13 (01)

[37] Study on the wear performance of high-speed railway brake materials at low temperatures under continuous braking conditions [J].

Ma, Lei ;

Ding, Siyuan ;

Zhang, Chao ;

Huang, YongZhi ;

Zhang, Xun .

WEAR, 2023, 512

[38] Role of secondary phase particles in fatigue behavior of high-speed railway gearbox material [J].

Jiao, Yinan ;

Zhang, Yifan ;

Ma, Shiqing ;

Sang, Deli ;

Zhang, Yang ;

Zhao, Jinjin ;

Liu, Yongqiang ;

Yang, Shaopu .

INTERNATIONAL JOURNAL OF FATIGUE, 2020, 131

[39] Wear Behavior of High-Speed Wheel and Rail Steels under Various Hardness Matching [J].

Shi, Xiao-jiao ;

Zhang, Xiao-xin ;

Diao, Gui-jiang ;

Yan, Qing-zhi .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (01) :366-380

[40] The Dynamic Tensile Behavior of Railway Wheel Steel at High Strain Rates [J].

Jing, Lin ;

Han, Liangliang ;

Zhao, Longmao ;

Zhang, Ying .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2016, 25 (11) :4959-4966

← 1 2 3 4 5 →