The Effect of Temperature to CTAB-assisted Solvothermal Synthesis of TiO2

Surface area has significant impact on the photocatalytic activity of semiconductor material. It was found that templates as structure directing agent played a role in regulating the surface area of materials. The most widely used as template is cetyltrimethylammonium bromide (CTAB) surfactant. In this research, TiO2 was prepared by solvothermal method used temperature variations of 150, 175, 200, and 225 degrees C. The X-ray powder diffraction (XRD) data indicated that anatase phase of TiO2 was successfully obtained with I4(1)/amd space group and as the synthesis temperature was increased, the crystallinity increases. The spectra infrared spectroscopy (IR) showed the broad peak situated at wavenumber 400-800 cm(-1) which was assigned to the stretching Ti-O vibration. Raman spectra showed peaks at wavenumber 145, 197, 397, 516, and 639 cm(-1) which were attributed to vibration modes of anatase The scanning electron microscopy (SEM) image demonstrated the morphology particle has homogeneous distribution and irregular shape. Furthermore, Brunauer-Emmett-Teller (BET) specific surface area showed the CTAB-assisted TiO2 which was synthesized at 175 degrees C has the highest surface area of 227.043 m(2)/g in this research among the others.