Study on the utilization of supersaturation degree in Al deoxidation to improve cleanliness and control of Al2O3 inclusions in ultra-low carbon steel

被引:1
|
作者
Ji, Yun-qing [1 ,2 ]
Jiang, Min [1 ]
Deng, Xiao-xuan [3 ]
Liu, Chun-yang [4 ]
Huang, Fu-xiang [3 ]
Wang, Xin-hua [1 ]
机构
[1] Univ Sci & Technol Beijing, Sch Met & Ecol Engn, 30 Xue Yuan Rd, Beijing 100083, Peoples R China
[2] Minist Ecol Environm, Chinese Acad Environm Planning, 10 Dayangfang,Beiyuan Rd, Chaoyang Dist 100012, Peoples R China
[3] Shougang Grp, Res Inst Technol, 69 Yang Zhuang Rd, Beijing 100043, Peoples R China
[4] Steelmaking Plant Beijing Shougang Co Ltd, Qian An City 100041, Hebei, Peoples R China
关键词
alumina; inclusion; deoxidation; supersaturation degree; ultra low carbon steel;
D O I
10.1051/metal/2021007
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Effects of supersaturation degree (S) in Al deoxidation on cleanliness and alumina inclusions in steel were studied. If enough Al was added to steel, higher initial dissolve oxygen before Al deoxidation resulted in higher steel cleanliness. In the experiments, with the rise of [mass% O] from 102 ppm to 340 ppm and 931 ppm, logS in steel melts were increased from 4.8, to 7.0 and 8.8, respectively. As a result, total oxygen (T.O) was decreased to 25 ppm, 22 ppm and 21 ppm, respectively. Based on the results, important influence of supersaturation degree on the formation of Al2O3 was revealed. At lower S, Al2O3 would be singular and smaller particles <= 5 mu m that was difficult to be removed. However, Al2O3 would exist as large clusters in steel at higher S, which can be efficiently removed. By utilizing the findings in laboratory, RH refining of ultra-low-carbon steel was optimized. Steel cleanness and control of inclusions were improved. As a result, surface defects in cold rolling sheets caused by Al2O3 inclusions were effectively minimized.
引用
收藏
页数:8
相关论文
共 50 条
  • [41] Recent Progress on Al2O3-C Refractories with Low/ultra-low Carbon Content:A Review
    ZHAO Chenrui
    YAN Mingwei
    LI Hongyu
    NIU Zhiwang
    LIANG Baoqing
    SHANG Junli
    China'sRefractories, 2022, 31 (01) : 35 - 44
  • [42] Formation mechanism and control of MgO·Al2O3 inclusions in non-oriented silicon steel
    Yan-hui Sun
    Ya-nan Zeng
    Rui Xu
    Kai-ke Cai
    International Journal of Minerals, Metallurgy, and Materials, 2014, 21 : 1068 - 1076
  • [43] Formation mechanism and control of MgO•Al2O3 inclusions in non-oriented silicon steel
    Sun, Yan-hui
    Zeng, Ya-nan
    Xu, Rui
    Cai, Kai-ke
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2014, 21 (11) : 1068 - 1076
  • [44] Formation mechanism and control of MgO·Al2O3 inclusions in non-oriented silicon steel
    Yan-hui Sun
    Ya-nan Zeng
    Rui Xu
    Kai-ke Cai
    International Journal of Minerals Metallurgy and Materials, 2014, 21 (11) : 1068 - 1076
  • [45] Study on Reducing Al2O3 Inclusions by Optimized Refining Slag
    Wang, Jun
    Wu, Guang-liang
    Ye, Ming-feng
    9TH INTERNATIONAL SYMPOSIUM ON HIGH-TEMPERATURE METALLURGICAL PROCESSING, 2018, : 633 - 642
  • [46] Kinetics Study on the Modification Process of Al2O3 Inclusions in High-Carbon Hard Wire Steel by Magnesium Treatment
    Xiong, Xingqiang
    Li, Changrong
    Xi, Zuobing
    Chen, Lu
    METALS, 2021, 11 (10)
  • [47] Preparation of ultra-fine MgO•Al2O3 spinel powder and its metallurgy behavior in low carbon steel
    Li, Yang
    Li, Shuang-jiang
    Zhuang, Ying
    Li, Wei-jian
    Jiang, Zhou-hua
    ADVANCED MATERIAL SCIENCE AND TECHNOLOGY, PTS 1 AND 2, 2011, 675-677 : 291 - 294
  • [48] Formation and Evolution Mechanism of the Inclusions of Al2O3•SiO2•CaO and Al2O3•SiO2•CaO•MgO in Seamless Steel Tube Steel
    Yang, Wenkui
    Yang, Jian
    Zhang, Runhao
    Sun, Han
    Song, Jingling
    Zhao, Yinghui
    Zhou, Xuan
    STEEL RESEARCH INTERNATIONAL, 2023, 94 (08)
  • [49] Simple identification of Al2O3 and MgO•Al2O3 spinel inclusions in steel using X-ray-excited optical luminescence
    Imashuku, Susumu
    Wagatsuma, Kazuaki
    X-RAY SPECTROMETRY, 2019, 48 (05) : 522 - 526
  • [50] Modification of MgO·Al2O3 spinel inclusions in Al-killed steel by Ca-treatment
    Shu-feng Yang
    Jing-she Li
    Zai-fei Wang
    Jiao Li
    Lin Lin
    International Journal of Minerals, Metallurgy, and Materials, 2011, 18 : 18 - 23