The influence of Nb on hot corrosion behavior of Ni-based superalloy at 800 °C in a mixture of Na2SO4-NaCl

被引：23

作者：

Weng, Fei ^{[1
]}

Yu, Huijun ^{[2
]}

Wan, Kai ^{[1
]}

Chen, Chuanzhong ^{[1
]}

机构：

[1] Shandong Univ, Dept Mat Sci & Engn, Key Lab Liquid Solid Struct Evolut & Proc Mat, Minist Educ, Jinan 250061, Shandong, Peoples R China

[2] Shandong Univ, Sch Mech Engn, Key Lab High efficiency & Clean Mech Manufacture, Minist Educ, Jinan 250061, Shandong, Peoples R China

来源：

JOURNAL OF MATERIALS RESEARCH | 2014年 / 29卷 / 21期

关键词：

HIGH-TEMPERATURE CORROSION; SINGLE-CRYSTAL SUPERALLOYS; FE-BASED SUPERALLOYS; OXIDATION BEHAVIOR; MECHANICAL-PROPERTIES; SO2-O2; ATMOSPHERES; NI-5AL COATINGS; AL-ALLOY; 900-DEGREES-C; RESISTANCE;

D O I：

10.1557/jmr.2014.282

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

New-type Ni-based superalloys with and without Nb were designed in this study. Their hot corrosion behaviors were investigated at 800 degrees C with the deposition of a mixture of Na2SO4 and NaCl. The corrosion kinetics was studied by thermogravimetry. Microstructure of the corrosion scales was studied by SEM and the phase constituent was analyzed by XRD. Results showed that the corrosion kinetics followed approximately parabolic law. The corrosion scales on the two Ni-based alloys were comprised of Cr2O3, Al2O3, TiO2, and NiCr2O4. NiO was only detected in the scale on alloy without Nb. Nb2O5 appeared with the addition of 2.0 wt% Nb. No sulfide emerged in the scales. The corrosion scales both exhibited a layered structure. With Nb addition, the hot corrosion resistance of the alloy was notably improved. The action mechanism of Nb was investigated extensively in this study.

引用

页码：2596 / 2603

页数：8

共 50 条

[31] Oxidation behavior of Ni-based superalloy GH738 in static air between 800 and 1000 °C
Wang, Jue
Xue, Hao
Wang, Ying
RARE METALS, 2021, 40 (03) : 616 - 625
[32] Influence of Silicon and Chromium on the Na2SO4-Induced Hot Corrosion Behavior of Titanium Alloys
Mitoraj-Krolikowska, Marzena
CRYSTALS, 2023, 13 (06)
[33] Severe Hot Corrosion of the Superalloy IN718 in Mixed Salts of Na2SO4 and V2O5 at 700 °C
Pradhan, Dhananjay
Mahobia, Girija Shankar
Chattopadhyay, Kausik
Singh, Vakil
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2018, 27 (08) : 4235 - 4243
[34] The Hot Corrosion of Fe-Mn-Al–C Alloy with NaCl/Na2SO4 Coating Mixtures at 750°C
C.-J. Wang
Y.-C. Chang
Y.-H. Su
Oxidation of Metals, 2003, 59 : 115 - 133
[35] The hot corrosion of Fe-Mn-Al-C alloy with NaCl/Na2SO4 coating mixtures at 750°C
Wang, CJ
Chang, YC
Su, YH
OXIDATION OF METALS, 2003, 59 (1-2): : 115 - 133
[36] High-throughput composition screening of Pt-modified aluminide coating for corrosion resistance in molten Na2SO4-NaCl salts at 900 °C
Li, Mengqi
Peng, Hui
Guo, Hongbo
SURFACE & COATINGS TECHNOLOGY, 2025, 505
[37] Influence of Pt-Al Coating on Hot Corrosion Resistance Behaviors of a Ni-Based Single-Crystal Superalloy
Wang Di
Wang Dong
Xie Guang
Wang Li
Dong Jiasheng
Chen Lijia
ACTA METALLURGICA SINICA, 2021, 57 (06) : 780 - 790
[38] The hot corrosion of 310 stainless steel with pre-coated NaCl/Na2SO4 mixtures at 750°C
Tsaur, CC
Rock, JC
Wang, CJ
Su, YH
MATERIALS CHEMISTRY AND PHYSICS, 2005, 89 (2-3) : 445 - 453
[39] AlxCoCrFeNi high entropy alloys with superior hot corrosion resistance to Na2SO4+25% NaCl at 900 °C
Li, Ling
Lu, Jie
Liu, Xuanzhen
Dong, Tao
Zhao, Xiaofeng
Yang, Fan
Guo, Fangwei
CORROSION SCIENCE, 2021, 187
[40] Grain size dependant high-temperature hot corrosion (HTHC) degradation behavior in Alloy 617 during exposure in Na2SO4 + NaCl + V2O5 salt mixture
Bhuyan, P.
Sanyal, S.
Mitra, R.
JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 914

← 1 2 3 4 5 →