The influence of Nb on hot corrosion behavior of Ni-based superalloy at 800 °C in a mixture of Na2SO4-NaCl

被引：23

作者：

Weng, Fei ^{[1
]}

Yu, Huijun ^{[2
]}

Wan, Kai ^{[1
]}

Chen, Chuanzhong ^{[1
]}

机构：

[1] Shandong Univ, Dept Mat Sci & Engn, Key Lab Liquid Solid Struct Evolut & Proc Mat, Minist Educ, Jinan 250061, Shandong, Peoples R China

[2] Shandong Univ, Sch Mech Engn, Key Lab High efficiency & Clean Mech Manufacture, Minist Educ, Jinan 250061, Shandong, Peoples R China

来源：

JOURNAL OF MATERIALS RESEARCH | 2014年 / 29卷 / 21期

关键词：

HIGH-TEMPERATURE CORROSION; SINGLE-CRYSTAL SUPERALLOYS; FE-BASED SUPERALLOYS; OXIDATION BEHAVIOR; MECHANICAL-PROPERTIES; SO2-O2; ATMOSPHERES; NI-5AL COATINGS; AL-ALLOY; 900-DEGREES-C; RESISTANCE;

D O I：

10.1557/jmr.2014.282

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

New-type Ni-based superalloys with and without Nb were designed in this study. Their hot corrosion behaviors were investigated at 800 degrees C with the deposition of a mixture of Na2SO4 and NaCl. The corrosion kinetics was studied by thermogravimetry. Microstructure of the corrosion scales was studied by SEM and the phase constituent was analyzed by XRD. Results showed that the corrosion kinetics followed approximately parabolic law. The corrosion scales on the two Ni-based alloys were comprised of Cr2O3, Al2O3, TiO2, and NiCr2O4. NiO was only detected in the scale on alloy without Nb. Nb2O5 appeared with the addition of 2.0 wt% Nb. No sulfide emerged in the scales. The corrosion scales both exhibited a layered structure. With Nb addition, the hot corrosion resistance of the alloy was notably improved. The action mechanism of Nb was investigated extensively in this study.

引用

页码：2596 / 2603

页数：8

共 50 条

[21] Electrochemical study on the hot corrosion behavior of Ni16Cr13Co4Mo alloy in molten NaCl-KCl and NaCl-KCl-Na2SO4
Wang, J. H.
Li, D. G.
Shao, T. M.
CORROSION SCIENCE, 2022, 200
[22] Hot corrosion studies on Ni-base superalloy at 650 °C under marine-like environment conditions using three salt mixture (Na2SO4 + NaCl + NaVO3)
Mannava, Venkateswararao
Rao, A. Sambasiva
Paulose, Neeta
Kamaraj, M.
Kottada, Ravi Sankar
CORROSION SCIENCE, 2016, 105 : 109 - 119
[23] Hot corrosion behavior of network structured TiBw/TA15 composite with Na2SO4 film at 800?C
Kang, Qingxin
Xu, Xiaoting
Wang, Guofeng
Luo, Shuyi
Zhan, Liqiang
MATERIALS CHARACTERIZATION, 2023, 195
[24] Hot corrosion behavior of a Si-Y co-deposition coating on a Ti2AlNb based alloy in NaCl-Na2SO4 mixture
Xiang, Jiayi
Xie, Faqin
Wu, Xiangqing
Wang, Shaoqing
Li, Lang
SURFACE & COATINGS TECHNOLOGY, 2021, 419
[25] Effect of microstructure on hot corrosion behavior of new superalloy Ad 730 in 75 wt% Na2SO4+25 wt% NaCl molten salt
Zhou, Qihang
An, Teng
Zhang, Kaiyu
Zhou, Chengshuang
Qian, Hangli
Ying, Danqing
Li, Yuhang
Zhang, Lin
MATERIALS LETTERS, 2023, 341
[26] Corrosion behavior of the NiCrAlY and NiSiAlY alloys with salt mixtures of NaCl/Na2SO4
Zheng, Haiyang
Cui, Tiancheng
Zhu, Bing
Yu, Xiaopeng
Yu, Miao
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A, 2024, 42 (02):
[27] Hot corrosion behavior of NiCr-Cr3C2-CaF2/BaF2 composite coating with NiAl bond coating in molten NaCl-KCl and NaCl-Na2SO4 at 800?
Wang, J. H.
Li, D. G.
Shao, T. M.
CORROSION SCIENCE, 2022, 206
[28] Hot corrosion behaviour of constant and pulsed current welded Hastelloy X in Na2SO4, V2O5, and NaCl salt mixture at 900 °C
Sathishkumar, M.
Manikandan, M.
Arivazhagan, N.
Arulmurugan, B.
Selvaraj, Senthil Kumaran
Vignesh, M.
Rajakumar, S.
Rajkumar, S.
MATERIALS RESEARCH EXPRESS, 2022, 9 (02)
[29] Microstructure and hot corrosion behavior of the Ni-based superalloy GH202 treated by laser shock processing
Cao, Jiangdong
Zhang, Junsong
Hua, Yinqun
Chen, Ruifang
Li, Zhibao
Ye, Yunxia
MATERIALS CHARACTERIZATION, 2017, 125 : 67 - 75
[30] Oxidation behavior of Ni-based superalloy GH738 in static air between 800 and 1000 °C
Jue Wang
Hao Xue
Ying Wang
Rare Metals, 2021, 40 : 616 - 625

← 1 2 3 4 5 →