Strength and fracture toughness of hot-pressed bulk Bi2Sr2Ca2Cu3Ox and Bi2Sr2Ca2Cu3Ox/Ag at 77 and 300 K

被引:13
|
作者
Salazar, A [1 ]
Pastor, JY [1 ]
Llorca, J [1 ]
机构
[1] Univ Politecn Madrid, Dept Mat Sci, ETS Ingn Caminos, E-28040 Madrid, Spain
来源
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS | 2003年 / 385卷 / 03期
关键词
BSCCO; 2223; BSCCO 2223/Ag composites; mechanical properties; cryogenic behavior; fracture; anisotropy;
D O I
10.1016/S0921-4534(02)02256-6
中图分类号
O59 [应用物理学];
学科分类号
摘要
A study was made of the effect of temperature (300 and 77 K) and orientation on the mechanical properties of bulk BSCCO 2223 and BSCCO 2223/Ag composites processed by hot-pressing. The unreinforced material was strongly textured and almost fully dense and its flexure strength was outstanding. The flexure strength of the composites showed the balance between the benefits due to the presence of Ag, and the harmful impact of higher porosity and reduced texture. The strength of all the materials was fairly independent of the orientation and temperature, although a noticeable improvement (6-20%) was found at 77 K when the crack propagation direction was parallel to the hot-press axis. The fracture toughness was mainly a function of the porosity with the dense, BSCCO 2223 material showing the highest value. In addition, the toughness was largely influenced by orientation and temperature, again reaching maximum (by up to 70%) in the specimens tested at 77 K with the crack plane parallel to the hot-press axis. This behavior was explained in terms of the crack deflection and of the toughening effect of ice. (C) 2002 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:404 / 414
页数:11
相关论文
共 50 条
  • [41] UPPER CRITICAL-FIELD AND ANISOTROPY OF THE HIGH-TC BI2SR2CA2CU3OX PHASE
    MATSUBARA, I
    TANIGAWA, H
    OGURA, T
    YAMASHITA, H
    KINOSHITA, M
    KAWAI, T
    PHYSICAL REVIEW B, 1992, 45 (13) : 7414 - 7417
  • [42] SCALING OF THE FLUX-PINNING FORCE IN EPITAXIAL BI2SR2CA2CU3OX THIN-FILMS
    YAMASAKI, H
    ENDO, K
    KOSAKA, S
    UMEDA, M
    YOSHIDA, S
    KAJIMURA, K
    PHYSICAL REVIEW LETTERS, 1993, 70 (21) : 3331 - 3334
  • [43] EFFECT OF OXYGEN PARTIAL-PRESSURE ON SUPERCONDUCTIVITY IN BI2SR1.5CA1.9CU3.4OX AND SYNTHESIS OF SINGLE-CRYSTALS OF UNDOPED BI2SR2CA2CU3OX (TC=108 K)
    STROBEL, P
    KORCZAK, W
    HODEAU, JL
    THOLENCE, JL
    PHYSICA C, 1989, 161 (02): : 155 - 166
  • [44] INSITU, RF PLASMA DEPOSITION OF BI2SR2CA2CU3OX THIN-FILMS AT ATMOSPHERIC-PRESSURE
    SHAH, A
    PATEL, S
    NARUMI, E
    SHAW, DT
    APPLIED PHYSICS LETTERS, 1993, 62 (19) : 2422 - 2424
  • [45] Bi2Sr2Ca2Cu3Ox超导体的低温内耗和相变的研究
    何思明
    林天时
    唐林昌
    陈志学
    吉晓洋
    低温物理学报, 1991, (03) : 182 - 185
  • [46] STRUCTURE AND PROPERTIES OF A BI2SR2CA2CU3OX-AG NANOCOMPOSITE
    ISHIDA, Y
    MATSUZAKI, J
    KIZUKA, T
    ICHINOSE, H
    PHYSICA C, 1991, 190 (1-2): : 67 - 69
  • [47] Analysis of the DC and AC behaviour of Bi2Sr2Ca2Cu3Ox tapes arranged in z-stack configuration
    Melini, A
    Tebano, R
    Mele, R
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2000, 340 (04): : 308 - 316
  • [48] EVIDENCE FOR PREFERENTIAL FORMATION OF THE (BI,PB)2SR2CA2CU3OX PHASE AT THE AG INTERFACE IN AG-SHEATHED (BI,PB)2SR2CA2CU3OX TAPES
    YI, F
    HIGH, YE
    LARBALESTIER, DC
    SUNG, YS
    HELLSTROM, EE
    APPLIED PHYSICS LETTERS, 1993, 62 (13) : 1553 - 1555
  • [49] MEASURE OF THE MAGNITUDE OF YOUNG MODULUS IN WHISKER-LIKE SAMPLES OF THE BI-BASED HIGH-TC MATERIALS BI2SR2CACU2OX AND BI2SR2CA2CU3OX
    TRITT, TM
    MARONE, M
    CHEN, XF
    SKOVE, MJ
    EHRLICH, AC
    TESSEMA, GX
    GILLESPIE, DJ
    FRANCK, JP
    JUNG, J
    PHYSICA C, 1991, 178 (4-6): : 296 - 300
  • [50] Examination of current limiting mechanisms in monocore Bi2Sr2Ca2Cu3Ox tape with high critical current density
    Polyanskii, A
    Feldmann, DM
    Patnaik, S
    Jiang, J
    Cai, X
    Larbalestier, D
    DeMoranville, K
    Yu, D
    Parrella, R
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2001, 11 (01) : 3269 - 3272