A study of the effect of aluminum on MoSi2 formation by self-propagation high-temperature synthesis

被引：17
作者：
Hasani, S. [1 ]
Panjepour, M. [1 ]
Shamanian, M. [1 ]
机构：
[1] Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran
来源：
JOURNAL OF ALLOYS AND COMPOUNDS | 2010年 / 502卷 / 01期
关键词：
Combustion synthesis; MoSi2; formation; Self-propagation high-temperature synthesis; Aluminum; The oxidation of aluminum; IN-SITU SYNTHESIS; COMBUSTION SYNTHESIS; COMPOSITES; AL;
D O I：
10.1016/j.jallcom.2010.04.159
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
In this study, the self-propagation high-temperature synthesis (SHS) for the formation of MoSi2 in the presence of aluminum was investigated. Test specimens with nominal compositions including (Mo + 2Si) with stoichiometric ratio and (Mo + 2Si)+ 5 wt% Al were employed. Each of the different samples was tested for SHS to determine the thermal profile and differential thermal analysis (DTA) under air atmosphere. The registered thermal profiles resulted for the two samples showed the maximum temperature increase (about 400 degrees C) in the combustion front in the presence of aluminum. The DTA results also showed that the area of silicon melting point on the DTA curve was deleted in the presence of aluminum. On the other hand, the X-ray diffraction (XRD), scanning electron microscope (SEM) and energy dispersive spectrometer (EDS) studies indicated that the SHS reaction between Mo and Si was done in a more complete manner in the presence of aluminum and aluminum particles were all oxidized. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码：80 / 86
页数：7
相关论文
共 50 条
[21]   Structure, Microhardness, and High-Temperature Oxidation Resistance of MoSi2 Alloys: Effect of Al Addition [J].
Putri, Ni Made Kesuma Astuti Indrianingsih ;
Suhandi, Andi ;
Hermanto, Bambang ;
Manawan, Maykel T. E. ;
Aritonang, Sovian ;
Sudiro, Toto .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2025,
[22]   Addition effects of aluminum and in situ formation of alumina in MoSi2 [J].
Guo-Jun Zhang ;
Xue-Mei Yue ;
Tadahiko Watanabe .
Journal of Materials Science, 1999, 34 :997-1001
[23]   Effect of Al and Cr alloying by arc cladding on the high-temperature oxidation resistance of MoSi2 materials [J].
Wang, Bin ;
Sun, ShunPing ;
Wang, HongJin ;
Li, XiaoPing ;
Lei, WeiNing .
MATERIALS RESEARCH EXPRESS, 2021, 8 (08)
[24]   Effect of sliding speed on wear property of MoSi2 at high temperature [J].
Zhang, Houan ;
Gu, Siyong .
MECHANICAL, MATERIALS AND MANUFACTURING ENGINEERING, PTS 1-3, 2011, 66-68 :150-154
[25]   Microstructure and Wear Performance of Cu-Mo-Si Alloys Fabricated by Self-Propagation High-Temperature Synthesis [J].
Xie, Hui ;
Jia, Lei ;
Wang, Siming ;
Zhu, Jiling ;
Lu, Zhenlin .
ECO-MATERIALS PROCESSING AND DESIGN XI, 2010, 658 :408-411
[26]   Self-Propagating High-Temperature Synthesis and Consolidation of MoSi2-MoB Heterophase Ceramics Alloyed with ZrB2 [J].
Pogozhev, Yu. S. ;
Potanin, A. Yu. ;
Rupasov, S. I. ;
Kiryukhantsev-Korneev, F. V. ;
Levashov, E. A. .
INTERNATIONAL JOURNAL OF SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS, 2023, 32 (03) :221-232
[27]   Effect of extra carbon addition on the self-propagation high-temperature synthesis characteristics of WO3-H3BO3-Mg-C system [J].
Omran, J. Ghorbantabar ;
Afarani, M. Shafiee ;
Sharifitabar, M. .
CERAMICS INTERNATIONAL, 2018, 44 (16) :20115-20121
[28]   Effects of combustion conditions on the characteristics of Al2O3/AlB12 composite powders produced by self-propagation high-temperature synthesis [J].
Liu, YH ;
Yin, S ;
Lai, HY .
JOURNAL OF INORGANIC MATERIALS, 2000, 15 (03) :473-479
[29]   Mechanical activation process for self-propagation high-temperature synthesis of ceramic-based compositesModeling and optimizing using response surface method [J].
M. Farhanchi ;
M. Neysari ;
R. Vatankhah Barenji ;
A. Heidarzadeh ;
R. Taherzadeh Mousavian .
Journal of Thermal Analysis and Calorimetry, 2015, 122 :123-133
[30]   Manufacturing of low cost MoSi2/Al2O3 composites by microwave activated self propagating high temperature Synthesis [J].
Sedghi, Arman ;
Noori, Nastarn Riahi .
JOURNAL OF CERAMIC PROCESSING RESEARCH, 2013, 14 (01) :41-44
12345