Influence of calcium on ignition-proof mechanism of AM50 magnesium alloy

被引：4
作者：
Cai, Huisheng [1 ]
Wang, Qudong [1 ]
Zhao, Yang [1 ]
Peng, Jianguo [1 ]
Zhang, Nannan [1 ]
Wang, Haichuan [2 ]
Suery, Michel [3 ]
Blandin, Jean Jacques [4 ]
机构：
[1] Shanghai Jiao Tong Univ, Natl Engn Res Ctr Light Alloy Net Forming, Sch Mat Sci & Engn, Shanghai 200240, Peoples R China
[2] Shanghai Weiyu High Sch, Shanghai 200031, Peoples R China
[3] Univ Grenoble Alpes, CNRS UMR5266, SIMaP, F-38402 St Martin Dheres, France
[4] Univ Grenoble Alpes, SIMaP, Grenoble INP, CNRS, F-38000 Grenoble, France
来源：
JOURNAL OF MATERIALS SCIENCE | 2022年 / 57卷 / 15期
基金：
中国国家自然科学基金;
关键词：
MG-CA ALLOYS; OXIDATION BEHAVIOR; Y ADDITIONS; RESISTANCE; CORROSION;
D O I：
10.1007/s10853-022-07151-6
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In order to improve the ignition proof of AM50 magnesium alloy, 1wt% Ca was added to AM50 magnesium alloy to prepare investigated alloy. The ignition temperature, ignition-proof holding time at the predetermined temperature, microstructure of oxide film and thermodynamics of oxide film formation were studied. The results show that after adding 1wt% Ca, the ignition temperature of AM50-1wt%Ca alloy reaches 832 degrees C, which is 248 degrees C higher than 584 degrees C of AM50 magnesium alloy. The holding time of AM50 alloy varies with temperature. The higher the temperature, the shorter the holding time. AM50 magnesium alloy can remain for about 720 s at 525 degrees C without ignition, while it only remains for about 50 s at 550 degrees C. The oxide film of AM50 magnesium alloy is mainly loose and porous MgO. The oxide film of AM50-1wt.%Ca alloy is a bilayer oxide film of MgO and CaO and CaO is mainly distributed in the outer layer of the oxide film. When the temperature is lower than 949 degrees C, the oG of CaO formation is less than that of MgO formation during the oxidation process of AM50-1wt%Ca alloy, MgO formed in the early stage of oxidation can be reduced to [Mg] by [Ca] and the minimum [Ca] content required for the reaction is always less than 1wt%. The dense bilayer oxide film formed on the surface of AM50-1wt%Ca alloy can effectively protect alloy and its oxidation process conforms to the parabola variation law.
引用
收藏
页码：7719 / 7728
页数：10
相关论文
共 30 条
  • [21] Oxidation resistance of Mg-9Al-1Zn alloys micro-alloyed with Be
    Tan, Qiyang
    Mo, Ning
    Jiang, Bin
    Pan, Fusheng
    Atrens, Andrej
    Zhang, Ming-Xing
    [J]. SCRIPTA MATERIALIA, 2016, 115 : 38 - 41
  • [22] The Ignition Behavior of a Ternary Mg-Sr-Ca Alloy
    Villegas-Armenta, Luis Angel
    Pekguleryuz, Mihriban Ozden
    [J]. ADVANCED ENGINEERING MATERIALS, 2020, 22 (05)
  • [23] Flame resistance and oxidation behavior of Mg-Y-Ce-Zr alloys
    Wang, Wenli
    Wang, Wei
    Wang, Qiang
    Zhang, Mengqi
    Wang, Along
    Li, Miaomiao
    [J]. MATERIALS RESEARCH EXPRESS, 2019, 6 (01)
  • [24] Recent developments and applications on high-performance cast magnesium rare-earth alloys
    Wu, Guohua
    Wang, Cunlong
    Sun, Ming
    Ding, Wenjiang
    [J]. JOURNAL OF MAGNESIUM AND ALLOYS, 2021, 9 (01) : 1 - 20
  • [25] The effect of calcium additions on the oxidation behavior in magnesium alloys
    You, BS
    Park, WW
    Chung, IS
    [J]. SCRIPTA MATERIALIA, 2000, 42 (11) : 1089 - 1094
  • [26] High temperature oxidation behavior of Mg-Y-Sn, Mg-Y, Mg-Sn alloys and its effect on corrosion property
    Yu, Xiaowen
    Jiang, Bin
    Yang, Hong
    Yang, Qingshan
    Xia, Xiangsheng
    Pan, Fusheng
    [J]. APPLIED SURFACE SCIENCE, 2015, 353 : 1013 - 1022
  • [27] In vitro corrosion of as-extruded Mg-Ca alloys-The influence of Ca concentration
    Zeng, Rong-Chang
    Qi, Wei-Chen
    Cui, Hong-Zhi
    Zhang, Fen
    Li, Shuo-Qi
    Han, En-Hou
    [J]. CORROSION SCIENCE, 2015, 96 : 23 - 31
  • [28] Behavior of surface oxidation on molten Mg-9Al-0.5Zn-0.3Be alloy
    Zeng, XQ
    Wang, QD
    Lü, YH
    Ding, WJ
    Zhu, YP
    Zhai, CQ
    Lu, C
    Xu, XP
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 301 (02): : 154 - 161
  • [29] Zeng XQ, 2001, J MATER PROCESS TECH, V112, P17, DOI 10.1016/S0924-0136(00)00854-2
  • [30] Effect of Mg-Nd Master Alloys on Ignition-proof Performance of AZ91D Magnesium Alloy
    Zhao, Weimin
    Zhao, Yang
    Wang, Zhifeng
    Li, Yongyan
    Ding, Jian
    Xue, Haitao
    [J]. ADVANCES IN KEY ENGINEERING MATERIALS, 2011, 214 : 118 - 121
123