High temperature oxidation behavior of Ti-Al-Nb ternary alloys

被引：50
作者：
Shen, Y [1 ]
Ding, XF
Wang, FG
Tan, Y
Yang, JM
机构：
[1] Dalian Univ Technol, Dept Mat Engn, Dalian 116024, Peoples R China
[2] Univ Calif Los Angeles, Dept Mat Sci & Engn, Los Angeles, CA 90095 USA
来源：
JOURNAL OF MATERIALS SCIENCE | 2004年 / 39卷 / 21期
关键词：
D O I：
10.1023/B:JMSC.0000044899.40687.a6
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The oxidation behavior of four Ti-Al-Nb ternary alloys with different microstructures were investigated at 1000 C using interrupted oxidation test in air. Alloys with single-phase gamma-TiAl, two-phase gamma-TiAl + alpha(2)-Ti3Al, multi-phase gamma-TiAl + alpha(2)-Ti3Al + Nb2Al and two-phase alpha(2)-Ti3Al + Nb2Al were prepared. The oxidation resistance of the Ti-Al-Nb ternary alloy at high temperature was found to be better than that of the binary Ti-Al alloy. Among the four Ti-Al-Nb ternary alloys, the gamma + alpha(2) two-phase alloy has the best oxidation resistance. The presence of Nb-enriched phase such as Nb2Al and Nb3Al decrease the oxidation resistance at elevated temperature presumably due to the formation of Nb2O5, which would accelerate the exfoliation of oxide. (C) 2004 Kluwer Academic Publishers.
引用
收藏
页码：6583 / 6589
页数：7
相关论文
共 32 条
[1]   EFFECT OF MO ADDITION ON THE OXIDATION BEHAVIOR OF TIAL INTERMETALLIC COMPOUND [J].
ANADA, H ;
SHIDA, Y .
MATERIALS TRANSACTIONS JIM, 1995, 36 (04) :533-539
[2]  
ANADA H, 1993, MAT T JIM, V34, P263
[3]  
ANADA H, 1994, J JAP I MET, V36, P745
[4]  
BHIDA Y, 1993, CORROS SCI, V35, P945
[5]  
Chen CH, 1998, CHEM VAPOR DEPOS, V4, P11, DOI 10.1002/(SICI)1521-3862(199801)04:01<11::AID-CVDE11>3.3.CO
[6]  
2-V
[7]  
CHEN LH, 1995, HOT WORKING TECHNOLO, V6, P7
[8]   Gamma titanium aluminide alloys - an assessment within the competition of aerospace structural materials [J].
Dimiduk, DM .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 263 (02) :281-288
[9]   Reply to the "Comment on 'Investigation on the 1000, 1150 and 1400°C isothermal section of the Ti-Al-Nb system'" -: Part II.: Modification of 1000 and 1150°C isothermal sections of the Ti-Al-Nb system [J].
Ding, JJ ;
Hao, SM .
INTERMETALLICS, 1998, 6 (04) :329-334
[10]   THE EFFECT OF MICROSTRUCTURE ON THE OXIDATION BEHAVIOR OF TIAL-BASED INTERMETALLICS [J].
GIL, A ;
HOVEN, H ;
WALLURA, E ;
QUADAKKERS, WJ .
CORROSION SCIENCE, 1993, 34 (04) :615-630
1234