Characterization of hybrid sol-gel coatings doped with hydrotalcite-like compounds to improve corrosion resistance of AA2024-T3 alloys

The inhibition effect of hydrotalcite addition to hybrid sol-gel coatings applied on AA2024-T3 alloy was evaluated. Hydrotalcite belongs to the anionic clay family with wide applications, most of them based on its anion exchange capacity due to its double layered structure. In this work hydrotalcite (HT) powder was prepared by the classical co-precipitation method using magnesium and aluminum nitrates as precursors. Different weight percentages (1, 5 and 10%, w/w) of hydrotalcite with Mg/Al ratio of 2.5 were added to hybrid sols prepared by copolymerization of 3-Glycydoxypropyltrimethoxysilane (GPTMS) and tetra-n-propoxyzirconium (TPOZ). The sol-gel coatings were deposited by dip-coating method on AA2024-T3 substrate. Scanning electron microscopy (SEM) and mechanical profilometry measurements revealed the heterogeneous particle sizes and the distribution of the agglomerates. Hydrotalcite additions significantly increased the bond strength between metal and coating, according to pull-off test results. The corrosion performance was evaluated by the salt spray fog chamber test and by Electrochemical Impedance Spectroscopy (EIS). The results showed a marked improvement of the corrosion resistance on the aluminum alloy when HT was added to the hybrid sol-gel coating. This positive effect was more evident at higher weight percentages of hydrotalcite. (C) 2009 Elsevier B.V. All rights reserved.