Material removal mechanisms by EDM of zirconia reinforced MWCNT nanocomposites

Several composites of tetragonal zirconia polycrystals doped with 3 mol% yttria (3Y-TZP) and multiwalled carbon nanotubes (MWCNT) with concentrations from 0.5 to 4 wt% CNT were processed, spark plasma sintered, and characterised for a wide range of mechanical, electrical and thermal properties. In particular, a strong increase in electrical conductivity at room temperature was found with only 0.5 wt% CNT. However, the thermal conductivity was decreasing with increasing CNT content. Electrical discharge machining (EDM) using die sinking was carried out using the composites of 1 and 2 wt% CNT as workpieces. It was shown that both compositions could be successfully machined by EDM. The surface integrity and the subsurface were studied by SEM/FIB in order to determine the material removal mechanisms, which were found to be associated to spalling and melting/evaporation. Raman Spectroscopy was used to evaluate the damage of CNTs after EDM. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.