Nanoscale-SiC doping for enhancing Jc and Hc2 in superconducting MgB2

被引:128
作者
Dou, SX [1 ]
Braccini, V
Soltanian, S
Klie, R
Zhu, Y
Li, S
Wang, XL
Larbalestier, D
机构
[1] Univ Wollongong, Inst Superconducting & Elect Mat, Wollongong, NSW 2522, Australia
[2] Univ Wisconsin, Appl Superconduct Ctr, Madison, WI 53706 USA
[3] Univ Wisconsin, Appl Conduct Ctr, Madison, WI 53706 USA
[4] Brookhaven Natl Lab, Upton, NY 11973 USA
[5] Nanyang Technol Univ, Adv Mat Res Ctr, Singapore 639798, Singapore
基金
澳大利亚研究理事会; 美国国家科学基金会;
关键词
D O I
10.1063/1.1814415
中图分类号
O59 [应用物理学];
学科分类号
摘要
The effect of nanoscale-SiC doping of MgB2 was investigated in comparison with undoped, clean-limit, and Mg-vapor-exposed samples using transport and magnetic measurements. It was found that there are two distinguishable but related mechanisms that control the critical current-density-field J(c)(H) behavior: increase of upper critical field H-c2 and improvement of flux pinning. There is a clear correlation between the critical temperature T-c, the resistivity rho, the residual resistivity ratio RRR=R(300 K)/R(40 K), the irreversibility field H*, and the alloying state in the samples. The H-c2 is about the same within the measured field range for both the Mg-vapor-treated and the SiC-doped samples. However, the J(c)(H) for the latter is higher than the former in a high-field regime by an order of magnitude. Mg vapor treatment induced intrinsic scattering and contributed to an increase in H-c2. SiC doping, on the other hand, introduced many nanoscale precipitates and disorder at B and Mg sites, provoking an increase of rho(40 K) from 1 muOmega cm (RRR=15) for the clean-limit sample to 300 muOmega cm (RRR=1.75) for the SiC-doped sample, leading to significant enhancement of both H-c2 and H* with only a minor effect on T-c. Electron energy-loss spectroscope and transmission electron microscope analysis revealed impurity phases: Mg2Si, MgO, MgB4, BOx, SixByOz, and BC at a scale below 10 nm and an extensive domain structure of 2-4-nm domains in the doped sample, which serve as strong pinning centers. (C) 2004 American Institute of Physics.
引用
收藏
页码:7549 / 7555
页数:7
相关论文
共 27 条
  • [21] Effect of SiO2 and SiC doping on the powder-in-tube processed MgB2 tapes
    Matsumoto, A
    Kumakura, H
    Kitaguchi, H
    Hatakeyama, H
    [J]. SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2003, 16 (08) : 926 - 930
  • [22] Maurin I, 2002, CHEM MATER, V14, P3894, DOI [10.1021/cm020308k, 10.1021/cm0203O8k]
  • [23] Effects of carbon doping on superconductivity in magnesium diboride
    Mickelson, W
    Cumings, J
    Han, WQ
    Zettl, A
    [J]. PHYSICAL REVIEW B, 2002, 65 (05) : 1 - 3
  • [24] Superconductivity at 39 K in magnesium diboride
    Nagamatsu, J
    Nakagawa, N
    Muranaka, T
    Zenitani, Y
    Akimitsu, J
    [J]. NATURE, 2001, 410 (6824) : 63 - 64
  • [25] Carbon doping of superconducting magnesium diboride
    Ribeiro, RA
    Bud'ko, SL
    Petrovic, C
    Canfield, PC
    [J]. PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 384 (03): : 227 - 236
  • [26] SERQUIS A, 2003, FALL M MRS BOST MA 1
  • [27] Intralayer carbon substitution in the MgB2 superconductor -: art. no. 134513
    Takenobu, T
    Ito, T
    Chi, DH
    Prassides, K
    Iwasa, Y
    [J]. PHYSICAL REVIEW B, 2001, 64 (13)