The corrosion behaviors of multilayer diamond-like carbon coatings: influence of deposition periods and corrosive medium

被引:52
作者
Cui, Mingjun [1 ,3 ]
Pu, Jibin [2 ]
Zhang, Guangan [1 ]
Wang, Liping [1 ,2 ]
Xue, Qunji [1 ,2 ]
机构
[1] Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China
[2] Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Key Lab Marine Mat & Related Technol, Ningbo 315201, Zhejiang, Peoples R China
[3] Univ Chinese Acad Sci, Beijing 100039, Peoples R China
基金
中国国家自然科学基金;
关键词
ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY; ION MASS-SPECTROMETRY; MECHANICAL-PROPERTIES; MODULATION PERIODS; MAGNESIUM ALLOY; STAINLESS-STEEL; DLC FILM; RESISTANCE; PERFORMANCE; EIS;
D O I
10.1039/c6ra05527c
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
Electrochemical measurements, salt spray tests and immersion tests were employed to investigate the influence of deposition periods and corrosive medium (NaCl, H2SO4, HCl, NaOH) on the corrosion behaviors of silicon doped multilayer diamond-like carbon (DLC) coatings. The results showed that the corrosion resistance of the multilayer DLC coatings was significantly improved with the increase of deposition periods. Interestingly, the coating with the highest deposition periods provided good corrosion protection in neutral and acidic solutions while poor corrosion protection in alkaline and acidic chloride solutions.
引用
收藏
页码:28570 / 28578
页数:9
相关论文
共 36 条
[1]   Time-of-flight secondary ion mass spectrometry: techniques and applications for the characterization of biomaterial surfaces [J].
Belu, AM ;
Graham, DJ ;
Castner, DG .
BIOMATERIALS, 2003, 24 (21) :3635-3653
[2]   SURFACE-ANALYSIS BY SECONDARY-ION MASS-SPECTROMETRY (SIMS) [J].
BENNINGHOVEN, A .
SURFACE SCIENCE, 1994, 299 (1-3) :246-260
[3]   Nitrogen doping for adhesion improvement of DLC film deposited on Si substrate by Filtered Cathodic Vacuum Arc (FCVA) technique [J].
Bootkul, D. ;
Supsermpol, B. ;
Saenphinit, N. ;
Aramwit, C. ;
Intarasiri, S. .
APPLIED SURFACE SCIENCE, 2014, 310 :284-292
[4]   Corrosion resistance of Ni/Cu/Ni-P triple-layered coating on Mg-Li alloy [J].
Chen, Dehua ;
Jin, Nan ;
Chen, Weiwei ;
Wang, Lu ;
Zhao, Shenqiang ;
Luo, Dawei .
SURFACE & COATINGS TECHNOLOGY, 2014, 254 :440-446
[5]   Corrosion behavior of copper under biofilm of sulfate-reducing bacteria [J].
Chen, Shiqiang ;
Wang, Peng ;
Zhang, Dun .
CORROSION SCIENCE, 2014, 87 :407-415
[6]   Deposition of Si-DLC film and its microstructural, tribological and corrosion properties [J].
Choi, Junho ;
Kawaguchi, Masahiro ;
Kato, Takahisa ;
Ikeyama, Masami .
MICROSYSTEM TECHNOLOGIES-MICRO-AND NANOSYSTEMS-INFORMATION STORAGE AND PROCESSING SYSTEMS, 2007, 13 (8-10) :1353-1358
[7]   AC impedance monitoring of pitting corrosion of stainless steel under a wet-dry cyclic condition in chloride-containing environment [J].
Cruz, RPV ;
Nishikata, A ;
Tsuru, T .
CORROSION SCIENCE, 1996, 38 (08) :1397-1406
[8]  
Cui M., 2015, RSC ADV, V5
[9]  
Dobrzanski L.A., 2007, Arch. Mater. Sci. Eng., V28, P12
[10]   Corrosion resistance of multilayer coatings deposited by PVD techniques onto the brass substrate [J].
Dobrzanski, LA ;
Lukaszkowicz, K ;
Zarychta, A ;
Cunha, L .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2005, 164 :816-821