Catalytic production of elemental sulfur from the thermal decomposition of H2S in the presence of CO2

被引:3
作者
Soriano, D
Keener, TC [1 ]
Khang, SJ
机构
[1] Univ Cincinnati, Dept Civil & Environm Engn, Cincinnati, OH 45221 USA
[2] Univ Cincinnati, Dept Chem Engn, Cincinnati, OH 45221 USA
关键词
sulfur; H2S; CO2; catalyst; Co-Mo; decomposition;
D O I
10.1080/00986449608936434
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
The feasibility of using a cobalt-molybdenum (Co-Mo) sulfide catalyst that was prepared from a commercial Co-Mo oxide catalyst for the production of elemental sulfur from hydrogen sulfide (H2S) and carbon dioxide (CO2) in a packed bed catalytic reactor was studied. It was demonstrated that the desired sulfide catalyst could be prepared by first reducing, then sulphiding the corresponding oxide. The results showed that the prepared catalyst was capable of producing elemental sulfur from the thermal decomposition of H2S in the presence of CO2 over a temperature range of 465-700 degrees C and at atmospheric pressure. A specific rate coefficient was calculated as well as the Arrhenius parameters for the non-equilibrated reaction. The H2S decomposition reaction was found to be a second order reaction and have an activation energy of 114.4 kJ/mol (27.3 kcal/mol).
引用
收藏
页码:73 / 89
页数:17
相关论文
共 50 条
[41]   Protic Ionic Liquids for the Selective Absorption of H2S from CO2: Thermodynamic Analysis [J].
Huang, Kuan ;
Zhang, Xiao-Min ;
Xu, Yun ;
Wu, You-Ting ;
Hu, Xing-Bang ;
Xu, Yun .
AICHE JOURNAL, 2014, 60 (12) :4232-4240
[42]   Corrosion behavior about tubing steel in environment with high H2S and CO2 content [J].
Li Wenfei ;
Zhou Yanjun ;
Xue Yan .
JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2013, 28 (05) :1038-1043
[43]   Decoupling Effects and Decomposition Analysis of CO2 Emissions from Thailand's Thermal Power Sector [J].
Muangthai, Isara ;
Lewis, Charles ;
Lin, Sue J. .
AEROSOL AND AIR QUALITY RESEARCH, 2014, 14 (07) :1929-1938
[44]   Upcycling acid waste gas containing H2S and CO2 into syngas and sulfur by non-thermal plasma coupled with Zn-Mo/Al2O3 catalyst [J].
Feng, Wenshuang ;
Yuwen, Xiaomeng ;
Mu, Xiaoliang ;
Zhao, Lu ;
Fang, Kegong .
FUEL, 2025, 381
[45]   CO2 Methanation in the Presence of Ce-Promoted Alumina Supported Nickel Catalysts: H2S Deactivation Studies [J].
Gac, Wojciech ;
Zawadzki, Witold ;
Rotko, Marek ;
Slowik, Grzegorz ;
Greluk, Magdalena .
TOPICS IN CATALYSIS, 2019, 62 (5-6) :524-534
[46]   H2S/CO2 separation using sterically hindered amine membranes [J].
Rao, Shraavya ;
Han, Yang ;
Ho, W. S. Winston .
JOURNAL OF MEMBRANE SCIENCE, 2023, 686
[47]   Gas Hydrate Formation Process for Simultaneously Capture of CO2 and H2S [J].
Xia, Zhiming ;
Li, Ze-Yu ;
Cai, Jing ;
Zhang, Yu ;
Wang, Yi ;
Yan, Kefeng ;
Chen, Zhaoyang ;
Li, Xiaosen .
INNOVATIVE SOLUTIONS FOR ENERGY TRANSITIONS, 2019, 158 :5705-5710
[48]   CO2 and H2S binary sorption on polyamine modified fumed silica [J].
Yoosuk, Boonyawan ;
Wongsanga, Tippayarat ;
Prasassarakich, Pattarapan .
FUEL, 2016, 168 :47-53
[49]   CO2/CH4 and H2S/CO2 Selectivity by Ionic Liquids in Natural Gas Sweetening [J].
Wang, Lan-yun ;
Xu, Yong-liang ;
Li, Zhen-dong ;
Wei, Ya-nan ;
Wei, Jian-ping .
ENERGY & FUELS, 2018, 32 (01) :10-23
[50]   Investigation of the corrosion inhibition performances of various inhibitors for carbon steel in CO2 and CO2/H2S environments [J].
Zhang, Chen ;
Asl, Vahdat Zahedi ;
Lu, Yuan ;
Zhao, Jingmao .
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2020, 55 (07) :531-538