Inhibition of copper corrosion by silane coatings

被引：136

作者：

Zucchi, F ^{[1
]}

Grassi, V ^{[1
]}

Frignani, A ^{[1
]}

Trabanelli, G ^{[1
]}

机构：

[1] Univ Ferrara, Dept Chem, Corros Study Ctr A Dacco, I-44100 Ferrara, Italy

来源：

CORROSION SCIENCE | 2004年 / 46卷 / 11期

关键词：

copper; corrosion; electrochemical tests; silane agents; mercapto group;

D O I：

10.1016/j.corsci.2004.03.019

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

OFHC copper specimens were pre-filmed in hydro-alcoholic solutions of various silanic agents (3-mercapto-propyl-trimethoxy-silane, PropS-SH; bis-triethoxy-silyi-ethane, BTSE; n-octadecyl-trimethoxy-silane, OctadecS; phenyl-trimethoxy-silane, PhS) to evaluate the influence of the silane molecule structure towards copper corrosion protection. Linear polarization resistance, potentiodynamic polarization curves, and electrochemical impedance spectroscopy tests were performed in 0.6 M NaCl. The thiolate bond caused a good anchoring of the silane molecule on the copper surface, which determined a noticeable hindrance to the anodic reaction of copper oxidation. Since this bond was found to be stronger than that of the oxane bond, the PropS-SH coating was more corrosion resistant and more persistent than the other tested silane coatings. The optimum pre-treatment solution pH was 4, although PropS-SH coating presented some imperfections. At this pH the coating was thicker than that at pH 10, when the silanized layer completely covered the copper surface. Nevertheless, the defects of this layer were so small that they could be plugged, for a prolonged time, by the copper corrosion products. (C) 2004 Elsevier Ltd. All rights reserved.

引用

页码：2853 / 2865

页数：13

共 21 条

[1] The inhibitive action of metacryloxypropylmethoxysilane (MAOS) on aluminium corrosion in NaCl solutions [J].

Beccaria, AM ;

Chiaruttini, L .

CORROSION SCIENCE, 1999, 41 (05) :885-899

[2] Inhibitory action of 3-trimethoxysilylpropanethiol-1 on copper corrosion in NaCl solutions [J].

Beccaria, AM ;

Bertolotto, C .

ELECTROCHIMICA ACTA, 1997, 42 (09) :1361-1371

[3] ELECTROCHEMICAL-BEHAVIOR OF COPPER IN NEUTRAL AERATED CHLORIDE SOLUTION .1. STEADY-STATE INVESTIGATION [J].

DESLOUIS, C ;

TRIBOLLET, B ;

MENGOLI, G ;

MUSIANI, MM .

JOURNAL OF APPLIED ELECTROCHEMISTRY, 1988, 18 (03) :374-383

[4]

DUARTE R, 2002, P 15 INT CORR C GRAN

[5] Corrosion mechanisms and products of copper in aqueous solutions at various pH values [J].

Feng, Y ;

Siow, KS ;

Teo, WK ;

Tan, KL ;

Hsieh, AK .

CORROSION, 1997, 53 (05) :389-398

[6] Effect of bath concentration and curing time on the structure of nonfunctional thin organosilane layers on aluminium [J].

Franquet, A ;

Le Pen, C ;

Terryn, H ;

Vereecken, J .

ELECTROCHIMICA ACTA, 2003, 48 (09) :1245-1255

[7] Chemical modification of an alkanethiol self-assembled layer to prevent corrosion of copper [J].

Haneda, R ;

Nishihara, H ;

Aramaki, K .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1997, 144 (04) :1215-1221

[8] Effect of chain length on the protection of copper by n-alkanethiols [J].

Jennings, GK ;

Munro, JC ;

Yong, TH ;

Laibinis, PE .

LANGMUIR, 1998, 14 (21) :6130-6139

[9] COMPARISON OF THE STRUCTURES AND WETTING PROPERTIES OF SELF-ASSEMBLED MONOLAYERS OF NORMAL-ALKANETHIOLS ON THE COINAGE METAL-SURFACES, CU, AG, AU [J].

LAIBINIS, PE ;

WHITESIDES, GM ;

ALLARA, DL ;

TAO, YT ;

PARIKH, AN ;

NUZZO, RG .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1991, 113 (19) :7152-7167

[10] CORROSION BEHAVIOR OF STEEL PRETREATED WITH SILANES [J].

LEIDHEISER, H ;

DECOSTA, M ;

GRANATA, RD .

CORROSION, 1987, 43 (06) :382-387

← 1 2 3 →