Influence of Activated Fluxes on the Bead Shape of A-TIG Welds on Carbon and Low-Alloy Steels in Comparison with Stainless Steel AISI 304L

被引：11
作者：
Niagaj, Jerzy [1 ]
机构：
[1] Lukasiewicz Res Network Inst Welding, Welding Technol Dept, PL-44100 Gliwice, Poland
来源：
METALS | 2021年 / 11卷 / 04期
关键词：
A-TIG; A-GTAW; depth of penetration; macrostructure; S235JR+N; P265GH; WELDOX; 1300; AISI; 304L; PENETRATION;
D O I：
10.3390/met11040530
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The article presents results of comparative A-TIG welding tests involving selected unalloyed and fine-grained steels, as well as high-strength steel WELDOX 1300 and austenitic stainless steel AISI 304L. The tests involved the use of single ingredient activated fluxes (Cr2O3, TiO2, SiO2, Fe2O3, NaF, and AlF3). In cases of carbon and low-alloy steels, the tests revealed that the greatest increase in penetration depth was observed in the steels which had been well deoxidized and purified during their production in steelworks. The tests revealed that among the activated fluxes, the TiO2 and SiO2 oxides always led to an increase in penetration depth during A-TIG welding, regardless of the type and grade of steel. The degree of the aforesaid increase was restricted within the range of 30% to more than 200%.
引用
收藏
页数：13
相关论文
共 16 条
[1]   Influence of Oxides on Microstructures and Mechanical Properties of High-Strength Steel Weld Joint [J].
Cai, Yangchuan ;
Luo, Zhen ;
Huang, Zunyue ;
Zeng, Yida .
HIGH TEMPERATURE MATERIALS AND PROCESSES, 2016, 35 (10) :1047-1053
[2]  
FAN D, 2001, T JWRI, V30, P35
[3]  
HEIPLE CR, 1982, WELD J, V61, pS97
[4]  
Kaijalainen A., 2012, P 8 INT C CLEAN STEE
[5]  
Kaushik, 2016, INT J ENG SCI INVENT, V2, P727
[6]   Effects of welding parameters on penetration depth in mild steel A-TIG welding [J].
Kurtulmus, M. .
SCIENTIA IRANICA, 2019, 26 (03) :1400-1404
[7]  
Lomzik M., 2020, BIUL I SPAW RES, V3, P9, DOI [10.17729/ebis.2020.3/1, DOI 10.17729/EBIS.2020.3/1]
[8]   Marangoni effects in welding [J].
Mills, KC ;
Keene, BJ ;
Brooks, RF ;
Shirali, A .
PHILOSOPHICAL TRANSACTIONS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES, 1998, 356 (1739) :911-925
[9]   Effect of A-TIG welding on deformation of austenitic steel components [J].
Niagaj, Jerzy .
Welding International, 2013, 27 (11) :853-856
[10]  
Niagaj J., 2003, Welding International, V17, P257, DOI 10.1533/wint.2003.3110
12