Effects of Alkali and Heat Treatment on Bioactivity of Micro-Arc Oxidized Coating on Ti6Al4V Alloy

被引：0

作者：

Wang Mingrun ^{[1
]}

Yang Sen ^{[1
]}

Wang Sanjun ^{[1
]}

机构：

[1] Inner Mongolia Univ Technol, Dept Mat Sci & Engn, Hohhot 010051, Peoples R China

来源：

RARE METAL MATERIALS AND ENGINEERING | 2009年 / 38卷 / 12期

关键词：

bioactivity; micro-arc oxidation; HA; heat treatment;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Porous TiO2 coating containing calcium and phosphate was prepared on Ti6Al4V alloy substrate using micro-arc oxidation, which was termed as MAO. And the MAO coating was treated by alkali and annealing, which was termed as MAONH. The morphology, element content and phase composition of the two kinds of coatings were analyzed by SEM, EDS and XRD, respectively. The results show that the MAONH coating is mainly composed of anatase, rutile and CaTiO3 phases, which is very different from the MAO coating. It is found that Ca2+ and P5+ ion deposit on the MAONH coating more easily than that on the MAO coating. The reason could be the hydrolysis of CaTiO3 soaking in Hank's solution, which results in abundant Ca2+ and Off ions. The apatite is deposited on the MAONH coating by ionic exchanges between OH-, Na+ ions of the MAONH coating and Ca2+, PO43- ions in the Hank's solution.

引用

页码：2212 / 2216

页数：5

共 16 条

[1]

DAN M, 2006, PROGR MODERN BIOMEDI, V6, P125

[2]

HUANG P, 2004, J CHINESE CERAMIC SO, V32, P1450

[3]

HUANG P, 2004, CHINESE J NONFERROUS, V14, P1565

[4]

Huang ZH, 2003, RARE METAL MAT ENG, V32, P277

[5]

LIANG FH, 2004, RARE METAL MAT ENG, V33, P1014

[6]

LU YP, 2001, J BIOMED ENG, V18, P451

[7]

MA C, 2007, J JIAMUSI U, V25, P52

[8]

REN Q, 2004, CHINA CERAMICS, V40, P35

[9] Microarc oxidation coatings formed on Ti6A14V in Na2SiO3 system solution:: Microstructure, mechanical and tribological properties [J].

Wang, Y. M. ;

Jiang, B. L. ;

Lei, T. Q. ;

Guo, L. X. .

SURFACE & COATINGS TECHNOLOGY, 2006, 201 (1-2) :82-89

[10] Characteristic and in vitro bioactivity of a microarc-oxidized TiO2-based coating after chemical treatment [J].

Wei, Daqing ;

Zhou, Yu ;

Jia, Dechang ;

Wang, Yaming .

ACTA BIOMATERIALIA, 2007, 3 (05) :817-827

← 1 2 →