Effect of the addition of YAG(Y3Al5O12) nanopowder on the mechanical properties of lanthanum zirconate

被引:34
作者
Li, J. Y.
Dai, H.
Zhong, X. H.
Zhang, Y. F.
Ma, X. F.
Meng, J.
Cao, X. Q. [1 ]
机构
[1] Chinese Acad Sci, Changchun Inst Appl Chem, Key Lab Rare Earth Chem & Phys, Changchun 130022, Jilin, Peoples R China
[2] Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2007年 / 460卷
关键词
nanocomposite; high-pressure sintering; toughening; fracture type;
D O I
10.1016/j.msea.2007.02.003
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
La2Zr2O7 (LZ) is a promising thermal barrier coating material for the high-temperature applications, which could be significantly toughened by the YAG nanopowder incorporated into the matrix. The composites of xYAG/(1-x)LZ (Y=10, 15, 20 vol. %, LZ-x-YAG) were densified by means of high-pressure sintering (HPS) under a pressure of 4.5 GPa at 1650 degrees C for 5 min, by which a high-relative density above 93% could be obtained. The morphologies of the fractured surfaces were investigated by the scanning electron microscope, and the fracture toughness and Vicker's-hardness of the composites were evaluated by the microindentation. The grain size of the LZ matrix drops significantly with the addition of YAG nanoparticles and the fracture type changes from the intergranular to a mixture type of the transgranular and intergranular in the nanocomposites. The LZ-20-YAG nanocomposite has a fracture toughness of 1.93 MPa m(1/2), which is obviously higher than that of the pure LZ (1.57 MPa m(1/2)), and the toughening mechanism is discussed in this paper. (C) 2007 Elsevier B.V. All rights reserved.
引用
收藏
页码:504 / 508
页数:5
相关论文
共 23 条
[1]   Ceramic materials for thermal barrier coatings [J].
Cao, XQ ;
Vassen, R ;
Stoever, D .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (01) :1-10
[2]  
Cao XQ, 2001, J AM CERAM SOC, V84, P2086, DOI 10.1111/j.1151-2916.2001.tb00962.x
[3]   Thermal diffusivity/microstructure relationship in Y-PSZ thermal barrier coatings [J].
Cernuschi, F ;
Bianchi, P ;
Leoni, M ;
Scardi, P .
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 1999, 8 (01) :102-109
[4]   FRACTURE TOUGHNESS DETERMINATIONS BY INDENTATION [J].
EVANS, AG ;
CHARLES, EA .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1976, 59 (7-8) :371-372
[5]   CERAMIC STEEL [J].
GARVIE, RC ;
HANNINK, RH ;
PASCOE, RT .
NATURE, 1975, 258 (5537) :703-704
[6]  
Grathwohl G., 1992, Journal of the European Ceramic Society, V10, P1, DOI 10.1016/0955-2219(92)90113-R
[7]   Transformation toughening in zirconia-containing ceramics [J].
Hannink, RHJ ;
Kelly, PM ;
Muddle, BC .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2000, 83 (03) :461-487
[8]   Fabrication of piezoelectric particle-dispersed ceramic nanocomposite [J].
Hwang, HJ ;
Nagai, T ;
Sando, M ;
Toriyama, M ;
Niihara, K .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1999, 19 (6-7) :993-997
[9]   CERAMICS DUCTILE AT LOW-TEMPERATURE [J].
KARCH, J ;
BIRRINGER, R ;
GLEITER, H .
NATURE, 1987, 330 (6148) :556-558
[10]   POLYCRYSTALLINE YTTRIUM-ALUMINUM-GARNET FIBERS FROM COLLOIDAL SOLS [J].
KING, BH ;
HALLORAN, JW .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1995, 78 (08) :2141-2148