Experimental data on fracture of open-hole composite laminates subjected to tension loading

被引：1
|
作者：
Ma, Zhaoyang [1 ,2 ]
Chen, Jianlin [2 ]
Li, Zheng [2 ]
Su, Xianyue [2 ]
机构：
[1] Shanghai Univ, Shanghai Inst Appl Math & Mech, Sch Mech & Engn Sci, Shanghai Key Lab Mech Energy Engn, Shanghai 200444, Peoples R China
[2] Peking Univ, Coll Engn, Dept Mech & Engn Sci, Beijing 100871, Peoples R China
来源：
DATA IN BRIEF | 2021年 / 35卷
基金：
中国国家自然科学基金;
关键词：
Fracture; Open-hole composite laminates; DIC; Different lay-ups; Tension;
D O I：
10.1016/j.dib.2021.106876
中图分类号：
O [数理科学和化学]; P [天文学、地球科学]; Q [生物科学]; N [自然科学总论];
学科分类号：
07 ; 0710 ; 09 ;
摘要：
In this data article, we present detailed failure process of big open-hole carbon fibre reinforced polymer (CFRP) composite laminates subjected to tension loading, which are tested by digital image correlation (DIC) system and electrical strain gauge system. In experiments, three different lay-ups are applied tension loading until specimens? failure. Several strain gages are distributed in different locations of specimens to measure strains during loading, at the same time, DIC is adopted to obtain field strains of specimens. The maximum force and failure modes of different lay-ups composite laminates are tested. The failure process is displayed by strain field images, and final failure images are also supplied in this article. Detailed numerical analysis are reported in [1] . (C) 2021 The Authors. Published by Elsevier Inc.
引用
收藏
页数：6
相关论文
共 50 条
  • [1] Progressive fracture analysis of the open-hole composite laminates: experiment and simulation
    Ma, Zhaoyang
    Chen, Jianlin
    Yang, Qingda
    Li, Zheng
    Su, Xianyue
    COMPOSITE STRUCTURES, 2021, 262
  • [2] Progressive fracture analysis of the open-hole composite laminates: experiment and simulation
    Ma, Zhaoyang
    Chen, Jianlin
    Yang, Qingda
    Li, Zheng
    Su, Xianyue
    Composite Structures, 2021, 262
  • [3] Simulating Initial and Progressive Failure of Open-Hole Composite Laminates under Tension
    Guo, Zhangxin
    Zhu, Hao
    Li, Yongcun
    Han, Xiaoping
    Wang, Zhihua
    APPLIED COMPOSITE MATERIALS, 2016, 23 (06) : 1209 - 1218
  • [4] The influence of non-traditional composite laminates on open-hole tension strength
    Stone, D. P.
    Smith, L. V.
    Kothidar, A.
    PROCEEDINGS OF THE ASME INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION 2007, VOL 10, PTS A AND B: MECHANICS OF SOLIDS AND STRUCTURES, 2008, : 757 - 762
  • [5] Simulating Initial and Progressive Failure of Open-Hole Composite Laminates under Tension
    Zhangxin Guo
    Hao Zhu
    Yongcun Li
    Xiaoping Han
    Zhihua Wang
    Applied Composite Materials, 2016, 23 : 1209 - 1218
  • [6] A finite fracture mechanics model for the prediction of the open-hole strength of composite laminates
    Camanho, P. P.
    Ercin, G. H.
    Catalanotti, G.
    Mahdi, S.
    Linde, P.
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2012, 43 (08) : 1219 - 1225
  • [7] Effect of tension damage on structures residual compression strength of open-hole composite laminates
    Wang X.
    Xia J.
    Ji Y.
    Cao D.
    Hu H.
    Li S.
    Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica, 2024, 41 (04): : 2111 - 2125
  • [8] Progressive damage analysis and experiments of open-hole composite laminates subjected to compression loads
    Liu, Zhengliang
    Yan, Leilei
    Wu, Zhen
    Zhou, Jie
    Wei, Haolin
    Zhang, Senlin
    Ren, Xiaohui
    ENGINEERING FAILURE ANALYSIS, 2023, 151
  • [9] Predicting the Residual Strength of Open-Hole (OH) Composite Specimens Subjected to Cyclic Loading
    Ceparano, Angelo
    Dell' Aversano, Raffaella
    VIII INTERNATIONAL CONFERENCE ON TIMES OF POLYMERS AND COMPOSITES: FROM AEROSPACE TO NANOTECHNOLOGY, 2016, 1736
  • [10] Material orthotropy effects on progressive damage analysis of open-hole composite laminates under tension
    Zhou, Song
    Sun, Yi
    Chen, Boyang
    Tay, Tong-Earn
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2017, 36 (20) : 1473 - 1486
12345