Formation of nickel, cobalt, copper, and iron aluminates from α- and γ-alumina-supported oxides:: A comparative study

被引:159
作者
Bolt, PH
Habraken, FHPM
Geus, JW
机构
[1] Univ Utrecht, Debye Inst, Dept Atom & Interface Phys, NL-3508 TA Utrecht, Netherlands
[2] Univ Utrecht, Dept Inorgan Chem, Debye Inst, NL-3508 TB Utrecht, Netherlands
关键词
D O I
10.1006/jssc.1997.7590
中图分类号
O61 [无机化学];
学科分类号
070301 ; 081704 ;
摘要
The rates of metal aluminate formation in MeOx/Al2O3 systems (Me = Ni, Co, Cu, Fe) at 500-1000 degrees C in O-2 or N-2 atmospheres were compared, using both alpha-Al2O3 and gamma-Al2O3 substrates. Interfacial reaction to MeAl2O4 was assessed using Rutherford backscattering spectrometry and X-ray diffraction. The lateral homogeneity of the samples was investigated using scanning electron microscopy, The spinel formation rate follows the sequence FeAl2O4 < NiAl2O4 < CoAl2O4 < CuAl2O4. This is explained in terms of thermodynamic limitations (FeAl2O4) and site-preference energies (CoAl2O4, NiAl2O4). The fast reaction to copper aluminate was accompanied by a severe rupture of the top layer (similar to 1 mu m) of the substrate, Penetration of transition metal ions into gamma-Al2O3 substrates is notable at considerably lower temperatures than with alpha-Al2O3 substrates, mainly due to grain boundary diffusion, Annealing conditions that favor the formation of transition metal cations of a low valency (Co-2+, Cu+) are beneficial for reactions to aluminates. (C) 1998 Academic Press.
引用
收藏
页码:59 / 69
页数:11
相关论文
共 31 条
[1]   A COMBINED STUDY BY XPS, RAMAN, DIFFUSE REFLECTANCE SPECTROSCOPY AND ANALYTICAL ELECTRON-MICROSCOPY OF THE INFLUENCE OF THE SEQUENCE OF IMPREGNATION ON THE STATE AND DISPERSION OF COBALT IN COMO-AL2O3 CATALYSTS [J].
APECETCHE, MA ;
HOUALLA, M ;
DELMON, B .
SURFACE AND INTERFACE ANALYSIS, 1981, 3 (02) :90-93
[2]  
Armijo J.S., 1969, Oxid. Met, V1, P171, DOI [10.1007/BF00603514, DOI 10.1007/BF00603514]
[3]   TEMPERATURE-PROGRAMMED REDUCTION OF COO/AL2O3 CATALYSTS [J].
ARNOLDY, P ;
MOULIJN, JA .
JOURNAL OF CATALYSIS, 1985, 93 (01) :38-54
[5]  
Barin I., 1973, THERMOCHEMICAL PROPE
[6]  
Barin Ihsan., 2013, THERMOCHEMICAL PROPE
[7]   INTERFACIAL REACTION OF NIO WITH AL2O3(11(2)OVER-BAR-0) AND POLYCRYSTALLINE ALPHA-AL2O3 [J].
BOLT, PH ;
LOBNER, SF ;
GEUS, JW ;
HABRAKEN, FHPM .
APPLIED SURFACE SCIENCE, 1995, 89 (04) :339-349
[8]   THE INTERACTION OF THIN NIO LAYERS WITH SINGLE-CRYSTALLINE ALPHA-AL2O3(11(2)OVER-BAR0) SUBSTRATES [J].
BOLT, PH ;
TENGROTENHUIS, E ;
GEUS, JW ;
HABRAKEN, FHPM .
SURFACE SCIENCE, 1995, 329 (03) :227-240
[9]   A RUTHERFORD BACKSCATTERING STUDY OF INTERFACIAL REACTIONS OF NICKEL AND COBALT OXIDES WITH ALUMINUM-OXIDE [J].
BOLT, PH ;
LOBNER, SF ;
VANDENBOUT, TP ;
GEUS, JW ;
HABRAKEN, FHPM .
APPLIED SURFACE SCIENCE, 1993, 70-1 (1 -4 pt A) :196-199
[10]  
CHERNAVSKII PA, 1993, KINET CATAL+, V34, P470