Synthesis and characterisation of nanoscale magnesium oxide powders and their application in thick films of Bi2Sr2CaCu2O8

被引：114

作者：

Bhargava, A ^{[1
]}

Alarco, JA ^{[1
]}

Mackinnon, IDR ^{[1
]}

Page, D ^{[1
]}

Ilyushechkin, A ^{[1
]}

机构：

[1] Univ Queensland, UniQuest Ltd ACD, St Lucia, Qld 4072, Australia

来源：

MATERIALS LETTERS | 1998年 / 34卷 / 3-6期

关键词：

synthesis; nanoscale; magnesium oxide; magnesite; high temperature superconductors; Bi2Sr2CaCu2O8; critical current;

D O I：

10.1016/S0167-577X(97)00148-1

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Nanoscale MgO powder was synthesized from magnesite ore by a wet chemical method. Acid dissolution was used to obtain a solution from which magnesium containing complexes were precipitated by either oxalic acid or ammonium hydroxide, The transformation of precipitates to the oxide was monitored by thermal analysis and XRD and the transformed powders were studied by electron microscopy. The MgO powders were added as dopants to Bi2SrCa2CuO8 powders and high temperature superconductor thick films were deposited on silver. Addition of suitable MgO powder resulted in increase of critical current density, J(c), from 8900 A cm(-2) to 13 900 A cm(-2) measured at 77 K and 0 T. The effect of MgO addition was evaluated by XRD, electron microscopy and critical current density measurements. (C) 1998 Elsevier Science B.V.

引用

页码：133 / 142

页数：10

共 50 条

[31] Kinetic roughening of magnetic flux fronts in Bi2Sr2CaCu2O8+δ crystals with columnar defects [J].

Barness, D. ;

Efraim, Y. ;

Taitelbaum, H. ;

Sinvani, M. ;

Shaulov, A. ;

Yeshurun, Y. .

PHYSICAL REVIEW B, 2012, 85 (17)

[32] Direct imaging of hot spots in Bi2Sr2CaCu 2O8+δ mesa terahertz sources [J].

Welp, U. (welp@anl.gov), 1600, American Institute of Physics Inc. (113)

[33] Structural and superconducting properties of Bi2-xPbxSr2CaCu2O8+δ [J].

Boekholt, M., 1600, Publ by Elsevier Science Publ BV (North-Holland), Amsterdam, Netherlands (185-89)

[34] Fluctuating stripes at the onset of the pseudogap in the high-Tc superconductor Bi2Sr2CaCu2O8+x [J].

Parker, Colin V. ;

Aynajian, Pegor ;

da Silva Neto, Eduardo H. ;

Pushp, Aakash ;

Ono, Shimpei ;

Wen, Jinsheng ;

Xu, Zhijun ;

Gu, Genda ;

Yazdani, Ali .

NATURE, 2010, 468 (7324) :677-680

[35] MAGNETIC-RELAXATION AND CRITICAL CURRENT IN BI2SR2CACU2O8+X SINGLE-CRYSTALS [J].

BALESTRINO, G ;

FIORANI, D ;

PAROLI, P ;

TEJADA, J ;

TESTA, AM .

JOURNAL OF SUPERCONDUCTIVITY, 1990, 3 (02) :211-214

[36] On the Causes of Degradation in Bi2Sr2CaCu2O8+x Round Wires and Coils by Quenching at 4.2 K [J].

Ye, Liyang ;

Cruciani, Davide ;

Effio, Timothy ;

Hunte, Frank ;

Schwartz, Justin .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2013, 23 (05)

[37] Evidence for a two step vortex matter melting in irradiated Bi2Sr2CaCu2O8+δ single crystals [J].

Shaidiuk, V. ;

Ammor, L. ;

Ruyter, A. .

SUPERCONDUCTIVITY CENTENNIAL CONFERENCE 2011, 2012, 36 :669-674

[38] Analysis of Critical Current Density in Bi2Sr2CaCu2O8+x Round Wire with Filament Fracture [J].

Liu, Donghui ;

Yong, Huadong ;

Zhou, Youhe .

JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, 2016, 29 (09) :2299-2309

[39] Interplay of superconductivity and bosonic coupling in the peak-dip-hump structure of Bi2Sr2CaCu2O8+δ [J].

Miller, Tristan L. ;

Zhang, Wentao ;

Ma, Jonathan ;

Eisaki, Hiroshi ;

Moore, Joel E. ;

Lanzara, Alessandra .

PHYSICAL REVIEW B, 2018, 97 (13)

[40] DC and AC susceptibility study of sol-gel synthesized Bi2Sr2CaCu2O8+δ superconductor [J].

Sharma, Devina ;

Kumar, Ranjan ;

Awana, V. P. S. .

CERAMICS INTERNATIONAL, 2013, 39 (02) :1143-1152

← 1 2 3 4 5 →