Effects of milling time and temperature on phase evolution of AISI316 stainless steel powder and subsequent sintering

被引:14
作者
Esmaeilzadeh, R. [1 ]
Salimi, M. [1 ]
Zamani, C. [1 ]
Hadian, A. M. [1 ]
Hadian, A. [1 ]
机构
[1] Univ Tehran, Coll Engn, Sch Met & Mat Engn, Tehran, Iran
关键词
AISI 316 stainless steel; Nano structure; Cryogenic milling; Microstructure; Sintering; Rietveld refinement; DEFORMATION-INDUCED MARTENSITE; STRAIN-INDUCED MARTENSITE; MECHANICAL-BEHAVIOR; MICROSTRUCTURAL EVOLUTION; NANOSTRUCTURED MATERIALS; PLASTIC-DEFORMATION; WEAR PROPERTIES; HIGH-STRENGTH; 304-STAINLESS-STEEL; TRANSFORMATION;
D O I
10.1016/j.jallcom.2018.06.325
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
In this study, effects of milling conditions on mechanical and microstructural properties of AISI 316 stainless steel powder were examined. Milling process was performed at ambient and cryogenic (-100 to -90 degrees C) temperatures for 1-12 h. The cryogenic tests were performed using liquid nitrogen without direct contact to the main powder. In order to investigate the effect of milling parameters on final properties of sintered samples, hot pressing was performed on selected as-milled powders at 1150 degrees C for 1 h under 65 MPa pressure. XRD analysis on as-milled powders confirmed the phase transformation of austenite (7) to a martensite in all samples. It was also evident from quantitative measurements carried out by Rietveld refinement method that the a weight fraction was a function of time and temperature. Based on this method, for all phases, crystallite size reduced to nanometer regime. Microstructural analysis for all samples was carried out by Scanning Electron Microscopy (SEM) equipped with Energy Dispersive Spectroscopy (EDS) that confirmed Rietveld analysis results. For as-sintered samples, relative density and Vickers hardness measurement were also performed to assess the physical and mechanical properties. (C) 2018 Elsevier B.V. All rights reserved.
引用
收藏
页码:341 / 348
页数:8
相关论文
共 47 条
[1]   Synthesis of austenitic stainless steel powder alloys by mechanical alloying [J].
Al-Joubori, Ahmed A. ;
Suryanarayana, C. .
JOURNAL OF MATERIALS SCIENCE, 2017, 52 (20) :11919-11932
[2]  
[Anonymous], STAND TEST METH TENS, DOI DOI 10.1520/C0273
[3]   316L stainless steel mechanical and tribological behavior-A comparison between selective laser melting, hot pressing and conventional casting [J].
Bartolomeu, F. ;
Buciumeanu, M. ;
Pinto, E. ;
Alves, N. ;
Carvalho, O. ;
Silva, F. S. ;
Miranda, G. .
ADDITIVE MANUFACTURING, 2017, 16 :81-89
[4]   QUANTITATIVE PHASE-ANALYSIS USING THE RIETVELD METHOD [J].
BISH, DL ;
HOWARD, SA .
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1988, 21 (02) :86-91
[5]   Temperature dependence of strain hardening and plastic instability behaviors in austenitic stainless steels [J].
Byun, TS ;
Hashimoto, N ;
Farrell, K .
ACTA MATERIALIA, 2004, 52 (13) :3889-3899
[6]  
Cullity B. D., ELEMENTS XRAY DIFFRA
[7]   Quantitative measurement of deformation-induced martensite in 304 stainless steel by X-ray diffraction [J].
De, AK ;
Murdock, DC ;
Mataya, MC ;
Speer, JG ;
Matlock, DK .
SCRIPTA MATERIALIA, 2004, 50 (12) :1445-1449
[8]  
Dieter GE, 2001, MECH METALLURGY
[9]  
El-Tahawy M., 2017, INFLUENCE PLASTIC DE, DOI [10.4028/www.scientific.net/MSF.885.13, DOI 10.4028/WWW.SCIENTIFIC.NET/MSF.885.13]
[10]   Electron backscattered diffraction study of ε/α′ martensitic variants induced by plastic deformation in 304 stainless steel [J].
Gey, N ;
Petit, B ;
Humbert, M .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2005, 36A (12) :3291-3299