Investigation of role of alloy microstructure in hydrogen-assisted fracture of AISI 4340 steel using circumferentially notched cylindrical specimens

被引:15
作者
Singh, Dhiraj Kumar [1 ,2 ,3 ]
Raman, R. K. Singh [3 ,4 ]
Maiti, S. K. [2 ]
Bhandakkar, Tanmay K. [2 ]
Pal, Sarvesh [5 ]
机构
[1] Indian Inst Technol, IITB Monash Res Acad, Powai 400076, India
[2] Indian Inst Technol, Dept Mech Engn, Powai 400076, India
[3] Monash Univ, Dept Mech & Aerosp Engn, Clayton, Vic 3800, Australia
[4] Monash Univ, Dept Chem Engn, Clayton, Vic 3800, Australia
[5] TEMCO, South32, TEMCO Rd, Bell Bay, Tas 7253, Australia
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2017年 / 698卷
关键词
Hydrogen-assisted cracking; Circumferentially notched tensile specimen; AISI; 4340; Cathodic charging; Hydrogen embrittlement; THRESHOLD STRESS INTENSITY; HIGH-STRENGTH STEEL; CRACKING K-ISCC; EMBRITTLEMENT; TOUGHNESS; ZONE;
D O I
10.1016/j.msea.2017.05.056
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The present study investigates the role of three different microstructures of a high strength steel AISI 4340 in relation to its susceptibility to hydrogen-assisted cracking (HAC), and demonstrates the ability of circumferential notch tensile (CNT) testing in distinguishing the role of the three microstructures. Critical stress intensity factors (SIFs) of CNT specimens of the steel with different microstructures (viz., the spheroidite (the as-received steel), the untempered martensite (the oil-quenched steel) and the tempered martensite (the oil-quenched + tempered steel)) were determined under two conditions at the room temperature, i.e., in air and under in-situ cathodic charging in 3.5% NaCl solution. The CNT tests under the two conditions show the as-received steel (with the spheroidite microstructure) to have a considerably high critical SIF (similar to 58 MPa m(0.5)) in air, and an insignificant decrease in critical SIF data when the test condition was changed to the cathodic charging, suggesting an insignificant susceptibility of the steel with the spheroidite microstructure to HAC. In contrast, the oil-quenching of the steel dramatically decreased the critical SIF to similar to 17 MPa m(0.5) in air, suggesting the highly strained martensitic microstructure to be more susceptible to cracking in air. The low critical SIF of the oil-quenched steel became even lower (similar to 10 MPa m (0.5)) under the cathodic charging condition, suggesting increased susceptibility of the martensitic microstructure to HAC. However, tempering of the martensitic microstructure at 300 degrees C for 2 h raised the critical SIF in air (by similar to 3 times), i.e., fracture resistance increased dramatically, but no significant improvement in the resistance to HAC was noticed. The hardness data of steels with the different microstructures are consistent with the trend in the corresponding SIF data. The study also provides two practical information: (a) an SIF below 10 MPa m(0.5) under operating load would avoid HAC in AISI 4340 steel in applications, and (b) the relatively new CNT technique is a viable low-cost testing option in assessing the role of microstructural variations in the context of HAC of high strength structural steels.
引用
收藏
页码:191 / 197
页数:7
相关论文
共 23 条
[1]  
[Anonymous], 2011, ASTM G1
[2]  
[Anonymous], 2015, ASTM E407
[3]  
ASTM ,, 2016, ASTM E8
[4]   Recent advances on hydrogen embrittlement of structural materials [J].
Dadfarnia, Mohsen ;
Nagao, Akihide ;
Wang, Shuai ;
Martin, May L. ;
Somerday, Brian P. ;
Sofronis, Petros .
INTERNATIONAL JOURNAL OF FRACTURE, 2015, 196 (1-2) :223-243
[5]   HYDROGEN-CONTROLLED CRACKING - APPROACH TO THRESHOLD STRESS INTENSITY [J].
GERBERICH, WW ;
CHEN, YT .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1975, 6 (02) :271-278
[6]   VALIDITY REQUIREMENTS FOR FRACTURE-TOUGHNESS MEASUREMENTS OBTAINED FROM SMALL CIRCUMFERENTIALLY NOTCHED CYLINDRICAL SPECIMENS [J].
IBRAHIM, RN ;
STARK, HL .
ENGINEERING FRACTURE MECHANICS, 1987, 28 (04) :455-460
[7]  
IBRAHIM RN, 1990, INT J FRACTURE, V44, P179
[8]  
Krauss G., 2015, STEELS PROCESS STRUC, P277
[9]   Mechanical properties and microstructural features of AISI 4340 high-strength alloy steel under quenched and tempered conditions [J].
Lee, WS ;
Su, TT .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1999, 87 (1-3) :198-206
[10]  
Liebowitz H., 1969, FRACTURE OF METALS A