Hydrothermal routes to various controllable morphologies of nanostructural lithium aluminate

被引：6

作者：

Hu, Linfeng ^{[1
]}

Qiao, Bin ^{[1
]}

Tang, Zilong ^{[1
]}

Zhang, Zhongtai ^{[1
]}

机构：

[1] Tsinghua Univ, Dept Mat Sci & Engn, State Key Lab New Ceram & Fine Proc, Beijing 100084, Peoples R China

来源：

MATERIALS RESEARCH BULLETIN | 2007年 / 42卷 / 08期

基金：

中国国家自然科学基金;

关键词：

A; nanostructures; B. chemical synthesis; C. electron microscopy; C. X-ray diffraction;

D O I：

10.1016/j.materresbull.2006.11.018

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The alpha-LiALO(2) powders have been successfully prepared by a hydrothermal route based on using the surfactant of heaxadecyltrimethyl ammonium bromide (CTAB) as the template. One-dimensional (1D) nanorods with higher and lower aspect ratio, 2D mesoporous microsheets were respectively observed with different concentration of the surfactants. A high specific surface area up to 151 m(2)/g was obtained by this method. The formation mechanism of the nanostructural lithium aluminate was proposed. (c) 2006 Elsevier Ltd. All rights reserved.

引用

页码：1407 / 1413

页数：7

共 19 条

[1] Dilute solution routes to various controllable morphologies of MCM-41 silica with a basic medium [J].

Cai, Q ;

Luo, ZS ;

Pang, WQ ;

Fan, YW ;

Chen, XH ;

Cui, FZ .

CHEMISTRY OF MATERIALS, 2001, 13 (02) :258-263

[2] Mophologies of vesicular silica templated by cationic surfactant with the auxiliary of diethyl ether [J].

Cui, K ;

Cai, Q ;

Chen, XH ;

Feng, QL ;

Li, HD .

MICROPOROUS AND MESOPOROUS MATERIALS, 2004, 68 (1-3) :61-64

[3]

Hou GY, 2004, RARE METAL MAT ENG, V33, P1351

[4]

JEFFEY SV, 2004, J COLLOID INTERF SCI, V269, P394

[5] Preparation of submicron size gamma lithium aluminate particles from the mixture of alumina sol and lithium salt by ultrasonic spray pyrolysis [J].

Kang, YC ;

Park, SB ;

Kwon, SW .

JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1996, 182 (01) :59-62

[6] Combustion synthesis of γ-lithium aluminate by using various fuels [J].

Li, F ;

Hu, K ;

Li, JL ;

Zhang, D ;

Chen, G .

JOURNAL OF NUCLEAR MATERIALS, 2002, 300 (01) :82-88

[7] H-titanate nanotube: a novel lithium intercalation host with large capacity and high rate capability [J].

Li, JR ;

Tang, ZL ;

Zhang, ZT .

ELECTROCHEMISTRY COMMUNICATIONS, 2005, 7 (01) :62-67

[8] Oxidation of a ZnS nanobelt into a ZnO nanotwin belt or double single-crystalline ZnO nanobelts [J].

Li, YJ ;

You, LP ;

Duan, R ;

Shi, PB ;

Qin, GG .

SOLID STATE COMMUNICATIONS, 2004, 129 (04) :233-238

[9] Ionic conductance behavior of polymeric composite solid electrolytes containing lithium aluminate [J].

Morita, M ;

Fujisaki, T ;

Yoshimoto, N ;

Ishikawa, M .

ELECTROCHIMICA ACTA, 2001, 46 (10-11) :1565-1569

[10] Release behavior of bred tritium from LiAlO2 [J].

Nishikawa, M ;

Kinjyo, T ;

Ishizaka, T ;

Beloglazov, S ;

Takeishi, T ;

Enoeda, M ;

Tanifuji, T .

JOURNAL OF NUCLEAR MATERIALS, 2004, 335 (01) :70-76

← 1 2 →