Influence of the casting processing route on the corrosion behavior of dental alloys

被引:15
作者
Galo, Rodrigo [1 ]
Rocha, Luis Augusto [2 ]
Faria, Adriana Claudia [1 ]
Silveira, Renata Rodrigues [1 ]
Ribeiro, Ricardo Faria [1 ]
Chiarello de Mattos, Maria da Gloria [1 ]
机构
[1] Univ Sao Paulo, Sch Dent Ribeirao Preto, Dept Dent Mat & Prosthodont, BR-14040904 Ribeirao Preto, Brazil
[2] Univ Minho, Ctr Mech & Mat Technol CT2M, Guimaraes, Portugal
来源
MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS | 2014年 / 45卷
基金
巴西圣保罗研究基金会;
关键词
Dental alloys; Corrosion; Casting; IN-VITRO; BIOCOMPATIBILITY; RESISTANCE; PALLADIUM; TITANIUM;
D O I
10.1016/j.msec.2014.10.006
中图分类号
TB3 [工程材料学]; R318.08 [生物材料学];
学科分类号
0805 ; 080501 ; 080502 ;
摘要
Casting in the presence of oxygen may result in an improvement of the corrosion performance of most alloys. However, the effect of corrosion on the casting without oxygen for dental materials remains unknown. The aim of this study was to investigate the influence of the casting technique and atmosphere (argon or oxygen) on the corrosion behavior response of six different dental casting alloys. The corrosion behavior was evaluated by electrochemical measurements performed in artificial saliva for the different alloys cast in two different conditions: arc melting in argon and oxygen-gas flame centrifugal casting. A slight decrease in open-circuit potential for most alloys was observed during immersion, meaning that the corrosion tendency of the materials increases due to the contact with the solution. Exceptions were the Co-based alloys prepared by plasma, and the Co-Cr-Mo and Ni-Cr-4Ti alloys processed by oxidized flame, in which an increase in potential was observed. The amount of metallic ions released into the artificial saliva solution during immersion was similar for all specimens. Considering the pitting potential, a parameter of high importance when considering the fluctuating conditions of the oral environment, Co-based alloys show the best performance in comparison with the Ni-based alloys, independent of the processing route. (C) 2014 Elsevier B.V. All rights reserved.
引用
收藏
页码:519 / 523
页数:5
相关论文
共 17 条
[1]  
Bergman M, 1986, Int Dent J, V36, P41
[2]   OSSEOINTEGRATED TITANIUM FIXTURES IN THE TREATMENT OF EDENTULOUSNESS [J].
BRANEMARK, PI ;
ADELL, R ;
ALBREKTSSON, T ;
LEKHOLM, U ;
LUNDKVIST, S ;
ROCKLER, B .
BIOMATERIALS, 1983, 4 (01) :25-28
[3]   Evaluation of titanium in oral conditions and its electrochemical corrosion behaviour [J].
Canay, S ;
Hersek, N ;
Culha, A ;
Bilgic, S .
JOURNAL OF ORAL REHABILITATION, 1998, 25 (10) :759-764
[4]   Castability optimization of palladium based alloys [J].
Cohen, SM ;
Kakar, A ;
Vaidyanathan, TK ;
Viswanadhan, T .
JOURNAL OF PROSTHETIC DENTISTRY, 1996, 76 (02) :125-131
[5]   Corrosion resistance properties of plasma nitrided Ti-6Al-4V alloy in nitric acid solutions [J].
Fossati, A ;
Borgioli, F ;
Galvanetto, E ;
Bacci, T .
CORROSION SCIENCE, 2004, 46 (04) :917-927
[6]   IN-VITRO CORROSION MEASUREMENTS OF DENTAL ALLOYS [J].
GEISGERSTORFER, J .
JOURNAL OF DENTISTRY, 1994, 22 (04) :247-251
[7]  
Khamis E, 1995, Int Dent J, V45, P209
[8]   Influence of micro-structure on corrosion behavior of a Ni-based superalloy in 3.5% NaCl [J].
Liu, Li ;
Li, Ying ;
Wang, Fuhui .
ELECTROCHIMICA ACTA, 2007, 52 (25) :7193-7202
[9]   The influence of alloy composition and casting procedure upon the corrosion behaviour of dental alloys: An in vitro study [J].
Mulders, C ;
Darwish, M ;
Holze, R .
JOURNAL OF ORAL REHABILITATION, 1996, 23 (12) :825-831
[10]   Use of x-ray photoelectron spectroscopy and cyclic polarization to evaluate the corrosion behavior of six nickel-chromium alloys before and after porcelain-fused-to-metal firing [J].
Roach, MD ;
Wolan, JT ;
Parsell, DE ;
Bumgardner, JD .
JOURNAL OF PROSTHETIC DENTISTRY, 2000, 84 (06) :623-634