Pore size effects on Ru/SiO2 catalysts with Mn and Zr promoters for Fischer-Tropsch synthesis

被引：22

作者：

Nurunnabi, Mohammad ^{[1
]}

Turn, Scott Q. ^{[1
]}

机构：

[1] Univ Hawaii Manoa, Hawaii Nat Energy Inst, Honolulu, HI 96822 USA

来源：

FUEL PROCESSING TECHNOLOGY | 2015年 / 130卷

关键词：

Pore size; Ru/SiO2; catalyst; Mn and Zr addition; Fischer-Tropsch synthesis; Catalyst activity; Deactivation rate; MGO SOLID-SOLUTION; PRESSURIZED CONDITIONS; COBALT CATALYSTS; NOBLE-METALS; PERFORMANCE; METHANE; SELECTIVITY; RESISTANCE; RU/AL2O3;

D O I：

10.1016/j.fuproc.2014.10.004

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

The effects of pore size on Ru/SiO2 catalyst performance were investigated for Fischer-Tropsch synthesis under the conditions of 503 K, 20 bar and 1800 h(-1). Ru/SiO2 with 10 nm pore size catalyst showed higher catalytic activity than Ru/SiO2 catalysts with 3, 6 and 30 nm pore sizes. The 10 nm pore size, Ru/SiO2 catalyst exhibited uniform pore diameter, an increased surface concentration of active Ru metals, and the increased dispersion of Ru on the surface compared to the other pore diameters. Deactivation was clearly observed for all Ru/SiO2 catalysts during the reaction. The addition of small amounts of Zr and Mn (1:30, Zr or Mn:Si) improved catalytic activity and stability for Fischer-Tropsch synthesis. The deactivation rate of Ru/Zr/Q10 was about 21% at 51 h time on stream and this rate was much lower than Ru/Q10 (57%). Ru/Mn/Q10 showed higher catalytic activity than Ru/Q10 and Ru/Zr/Q10, and its deactivation rate was much lower -9% after 51 h time on stream. The small amount of Mn added to the Ru/SiO2 increased the concentration of active Ru metals and enhanced their dispersion on the support surface. (C) 2014 Elsevier B.V. All rights reserved.

引用

页码：155 / 164

页数：10

共 50 条

[31] Fischer-Tropsch Reaction over Bimodal Porous Ru/SiO2 Catalysts Prepared by Alkoxide Method
Okabe, Kiyomi
Murata, Kazuhisa
Liu, Yangyong
JOURNAL OF THE JAPAN PETROLEUM INSTITUTE, 2010, 53 (02) : 106 - 110
[32] Effect of Resorcinol Formaldehyde Resin Gel on the Preparation of Co/SiO2 Catalysts for Fischer-Tropsch Synthesis
Chen Liang
Shen Jianyi
CHINESE JOURNAL OF CATALYSIS, 2012, 33 (04) : 621 - 628
[33] Effects of promoters on catalytic performance of Fe-Co/SiO2 catalyst for Fischer-Tropsch synthesis
Xiangdong Ma1
2. Shanghai Yankuang Energy RD Co.Ltd
3. School of Chemical Engineering
Journal of Natural Gas Chemistry, 2009, 18 (03) : 354 - 358
[34] Effects of nanotubes pore size on the catalytic performances of iron catalysts supported on carbon nanotubes for Fischer-Tropsch synthesis
Abbaslou, Reza M. Malek
Soltan, Jafar
Dalai, Ajay K.
APPLIED CATALYSIS A-GENERAL, 2010, 379 (1-2) : 129 - 134
[35] CO/SiO2 sol-gel catalysts for Fischer-Tropsch synthesis
Bianchi, CL
Martini, F
Moggi, P
CATALYSIS LETTERS, 2001, 76 (1-2) : 65 - 69
[36] Fischer-Tropsch synthesis over Co/SiO2 catalysts modified with ethylenediamine
Wang, Yuelun
Hou, Bo
Li, Debao
Chen, Jiangang
Sun, Yuhan
RENEWABLE AND SUSTAINABLE ENERGY II, PTS 1-4, 2012, 512-515 : 2143 - +
[37] Effects of promoters on catalytic performance of Fe-CO/SiO2 catalyst for Fischer-Tropsch synthesis
Ma, Xiangdong
Sun, Qiwen
Ying, Weiyong
Fang, Dingye
JOURNAL OF NATURAL GAS CHEMISTRY, 2009, 18 (03): : 354 - 358
[38] Cobalt supported on Zr-modified SiO2 as an efficient catalyst for Fischer-Tropsch synthesis
Wu, Y. J.
Zhang, W. T.
Yang, M. M.
Zhao, Y. H.
Liu, Z. T.
Yan, J. Y.
RSC ADVANCES, 2017, 7 (39): : 24157 - 24162
[39] Effects of Sm on Fe-Mn catalysts for Fischer-Tropsch synthesis
Han, Zhonghao
Qian, Weixin
Ma, Hongfang
Zhang, Haitao
Sun, Qiwen
Ying, Weiyong
RSC ADVANCES, 2019, 9 (55) : 32240 - 32246
[40] Mn-modified Ru Catalysts Supported on Carbon Nanotubes for Fischer-Tropsch Synthesis
Murata, Kazuhisa
Okabe, Ktyomt
Inaba, Megumu
Takahara, Isao
Liu, Yanyong
JOURNAL OF THE JAPAN PETROLEUM INSTITUTE, 2009, 52 (01) : 16 - 20

← 1 2 3 4 5 →