Pore size effects on Ru/SiO2 catalysts with Mn and Zr promoters for Fischer-Tropsch synthesis

被引：22
|
作者：
Nurunnabi, Mohammad [1 ]
Turn, Scott Q. [1 ]
机构：
[1] Univ Hawaii Manoa, Hawaii Nat Energy Inst, Honolulu, HI 96822 USA
来源：
FUEL PROCESSING TECHNOLOGY | 2015年 / 130卷
关键词：
Pore size; Ru/SiO2; catalyst; Mn and Zr addition; Fischer-Tropsch synthesis; Catalyst activity; Deactivation rate; MGO SOLID-SOLUTION; PRESSURIZED CONDITIONS; COBALT CATALYSTS; NOBLE-METALS; PERFORMANCE; METHANE; SELECTIVITY; RESISTANCE; RU/AL2O3;
D O I：
10.1016/j.fuproc.2014.10.004
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
The effects of pore size on Ru/SiO2 catalyst performance were investigated for Fischer-Tropsch synthesis under the conditions of 503 K, 20 bar and 1800 h(-1). Ru/SiO2 with 10 nm pore size catalyst showed higher catalytic activity than Ru/SiO2 catalysts with 3, 6 and 30 nm pore sizes. The 10 nm pore size, Ru/SiO2 catalyst exhibited uniform pore diameter, an increased surface concentration of active Ru metals, and the increased dispersion of Ru on the surface compared to the other pore diameters. Deactivation was clearly observed for all Ru/SiO2 catalysts during the reaction. The addition of small amounts of Zr and Mn (1:30, Zr or Mn:Si) improved catalytic activity and stability for Fischer-Tropsch synthesis. The deactivation rate of Ru/Zr/Q10 was about 21% at 51 h time on stream and this rate was much lower than Ru/Q10 (57%). Ru/Mn/Q10 showed higher catalytic activity than Ru/Q10 and Ru/Zr/Q10, and its deactivation rate was much lower -9% after 51 h time on stream. The small amount of Mn added to the Ru/SiO2 increased the concentration of active Ru metals and enhanced their dispersion on the support surface. (C) 2014 Elsevier B.V. All rights reserved.
引用
收藏
页码：155 / 164
页数：10
相关论文
共 50 条
  • [21] Promotion of CO/SiO2 Fischer-Tropsch catalysts with zirconium
    Moradi, GR
    Basir, MM
    Taeb, A
    Kiennemann, A
    CATALYSIS COMMUNICATIONS, 2003, 4 (01) : 27 - 32
  • [22] Comparison of induction behavior of Co/CNT and Co/SiO2 catalysts for the Fischer-Tropsch synthesis
    Bai, Suli
    Huang, Chengdu
    Lv, Jing
    Li, Zhenhua
    CATALYSIS COMMUNICATIONS, 2012, 22 : 24 - 27
  • [23] Gd promotion of CO/SiO2 Fischer-Tropsch synthesis catalysts
    Huber, GW
    Butala, SJM
    Lee, ML
    Bartholomew, CH
    CATALYSIS LETTERS, 2001, 74 (1-2) : 45 - 48
  • [24] Effects of Co/SiO2 Particle Size on Fischer-Tropsch Synthesis: Study by TPD and DRIFTS
    Qiu Chengwu
    Wu Baoshan
    Meng Shaocong
    Li Yongwang
    ACTA CHIMICA SINICA, 2015, 73 (07) : 690 - 698
  • [25] Fischer-Tropsch Synthesis on Co/SiO2 Catalysts with Potassium Promoter
    Atashi, Hossein
    Sahebi-shahemabadi, Mehdi
    Akhavan, Reza
    ASIAN JOURNAL OF CHEMISTRY, 2010, 22 (03) : 1925 - 1934
  • [26] Ruthenium Modification on Mn and Zr-Modified Co/SiO2 Catalysts for Slurry-Phase Fischer-Tropsch Synthesis
    Miyazawa, Tomohisa
    Hanaoka, Toshiaki
    Shimura, Katsuya
    Hirata, Satoshi
    CATALYSTS, 2015, 5 (01) : 26 - 37
  • [27] Fischer-Tropsch synthesis: The role of pore size for Co/SBA-15 catalysts
    Xiong, Haifeng
    Zhang, Yuhua
    Liew, Kongyong
    Li, Jinlin
    JOURNAL OF MOLECULAR CATALYSIS A-CHEMICAL, 2008, 295 (1-2) : 68 - 76
  • [28] Iron catalysts supported on carbon nanotubes for Fischer-Tropsch synthesis: effect of pore size
    Abbaslou, R. M. Malek
    Soltan, J.
    Sigurdson, S.
    Dalai, A. K.
    ENERGY AND SUSTAINABILITY II, 2009, 121 : 147 - 156
  • [29] Reliable pore size effect on Fischer-Tropsch synthesis over well-defined uniform pore-structure Fe2O3/SiO2 catalysts
    Yin, Fei
    Tan, Gui-ming
    Gao, Shi-mao
    Chen, Ai-cheng
    Chen, Hang
    Du, Yu-fei
    REACTION KINETICS MECHANISMS AND CATALYSIS, 2023, 136 (03) : 1301 - 1315
  • [30] Effect of Ru addition to CO/SiO2/HZSM-5 catalysts on Fischer-Tropsch synthesis of gasoline-range hydrocarbons
    Li, Yu-Ping
    Wang, Tie-Jun
    Wu, Chuang-Zhi
    Qin, Xin-Xin
    Tsubaki, Noritatsu
    CATALYSIS COMMUNICATIONS, 2009, 10 (14) : 1868 - 1874
12345