Corrosion Fatigue Crack Growth Behavior of Alloy 690 in High-Temperature Pressurized Water

被引：6
|
作者：
Chen, Kai [1 ]
Du, Donghai [1 ]
Zhang, Lefu [1 ]
Andresen, Peter L. [2 ]
机构：
[1] Shanghai Jiao Tong Univ, Sch Nucl Sci & Engn, Shanghai 200240, Peoples R China
[2] GE Global Res, One Res Circle CE 2513, Schenectady, NY 12309 USA
来源：
CORROSION | 2017年 / 73卷 / 06期
关键词：
Alloy; 690; corrosion fatigue; crack growth rate; modeling; orientation; threshold stress intensity; AUSTENITIC STAINLESS-STEELS; REACTOR CONDITIONS; ENVIRONMENT; HYDROGEN; IRON;
D O I：
10.5006/2324
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Corrosion fatigue crack growth behavior of Alloy 690 was investigated in air and high-temperature pressurized water environments. The stress intensity factor amplitude threshold (Delta K-th) was obtained, and the effects of stress intensity factor (Delta K), cyclic frequency (f), loading ratio (R), and material orientation on the corrosion fatigue crack growth rates were studied. The observed environmental acceleration on corrosion fatigue crack growth was quantitatively analyzed, and an empirical formula and the Ford-Andresen model were utilized to describe and explain the corrosion fatigue behavior of Alloy 690.
引用
收藏
页码：724 / 733
页数：10
相关论文
共 50 条
  • [41] Effects of heat treatment on corrosion fatigue and stress corrosion crack growth of additive-manufactured Alloy 800H in high-temperature water
    Yang, Jingfan
    Song, Miao
    Hawkins, Laura R.
    Liu, Xiang
    He, Lingfeng
    Lou, Xiaoyuan
    CORROSION SCIENCE, 2021, 191
  • [42] Effects of heat treatment on corrosion fatigue and stress corrosion crack growth of additive-manufactured Alloy 800H in high-temperature water
    Yang, Jingfan
    Song, Miao
    Hawkins, Laura R.
    Liu, Xiang
    He, Lingfeng
    Lou, Xiaoyuan
    Corrosion Science, 2021, 191
  • [43] Investigation of Fatigue Crack Propagation Behavior on the Surface of Machining Notches of Alloy 690TT in Simulated Pressurized Water Reactor Water
    Fu, Zhenghong
    Gou, Guoqing
    Xiao, Jun
    Qiu, Shaoyu
    Liu, Jinyun
    Zha, Wusheng
    Wang, Wanjing
    Yang, Yuping
    CORROSION, 2017, 73 (10) : 1258 - 1267
  • [44] Effect of TiN Inclusion on Fatigue Crack Growth Behavior of Alloy 690 Tube
    Chen Kai
    Du Donghai
    Lu Hui
    Zhang Lefu
    Shi Xiuqiang
    Xu Xuelian
    RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (04) : 1180 - 1184
  • [45] EFFECT OF FLOW-RATE ON FATIGUE CRACK-GROWTH BEHAVIOR OF A NUCLEAR PRESSURE-VESSEL STEEL IN HIGH-TEMPERATURE PRESSURIZED WATER
    KATADA, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1987, 73 (05): : S474 - S474
  • [46] FATIGUE CRACK-GROWTH BEHAVIOR OF PRESSURE-VESSEL STEELS AND SUBMERGED-ARC WELDMENTS IN A HIGH-TEMPERATURE PRESSURIZED WATER ENVIRONMENT
    LIAW, PK
    LOGSDON, WA
    BEGLEY, JA
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (10): : 2069 - 2085
  • [47] Constraint effect of corrosion fatigue crack growth behavior in S690 high strength steel
    Han Y.
    Li Z.
    Xu L.
    Jing H.
    Zhao L.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2018, 39 (12): : 13 - 18
  • [48] Corrosion fatigue damage mechanism and life evaluation of Inconel Alloy 690TT steam generator tube in high temperature pressurized water
    Li, Z. H.
    Lu, Y. H.
    Hong, C.
    Zhao, Y. G.
    Han, Y. M.
    Shoji, T.
    CORROSION SCIENCE, 2023, 212
  • [49] EFFECTS OF ENVIRONMENT ON HIGH-TEMPERATURE FATIGUE CRACK GROWTH IN A SUPER-ALLOY
    FLOREEN, S
    KANE, RH
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (11): : 1745 - 1751
  • [50] Role of TiN inclusion on corrosion fatigue behavior of Alloy 690 steam generator tubes in borated and lithiated high temperature water
    Tan, Jibo
    Wu, Xinqiang
    Han, En-Hou
    Ke, Wei
    Liu, Xiaoqiang
    Meng, Fanjiang
    Xu, Xuelian
    CORROSION SCIENCE, 2014, 88 : 349 - 359
12345