Detection of low cycle fatigue in type 316 stainless steel using HTS-SQUID

被引：2
|
作者：
Park, DG
Kim, DW
Timofeev, VP
Hong, JH
机构：
[1] Korea Atom Energy Res Inst, Taejon 305600, South Korea
[2] Verkin Inst Low Temp Phys & Eng, UA-61103 Kharkov, Ukraine
来源：
ADVANCES IN NONDESTRUCTIVE EVALUATION, PT 1-3 | 2004年 / 270-273卷
关键词：
type; 316; steel; low cycle fatigue; HTS SQUID; magnetic moment; susceptometer;
D O I：
10.4028/www.scientific.net/KEM.270-273.1224
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
A portable RF HTS SQUID-based susceptometer was applied to the measurement of fatigue behavior for type 316L(N) stainless steel containing 0.04% to 0.15% nitrogen content. Strain-controlled low cycle fatigue (LCF) tests were conducted at RT and 600 degreesC in air an atmosphere, and the magnetic moments were measured after the fatigue test using HTS SQUID. The magnetic moment of an as-received sample is higher than that of a fatigued sample in all the temperature ranges irrespective of the nitrogen content. The fatigue life decreased with an increasing test temperature up to 500 degreesC, but increased at 600 degreesC. The change of magnetic moments by LCF test is attributed to the stress induced micro defects.
引用
收藏
页码：1224 / 1228
页数：5
相关论文
共 50 条
  • [1] Development of Eddy Current Testing System Using HTS-SQUID on a Hand Cart for Detection of Fatigue Cracks of Steel Plate Used in Expressways
    Tsukamoto, Akira
    Hato, Tsunehiro
    Adachi, Seiji
    Oshikubo, Yasuo
    Tsukada, Keiji
    Tanabe, Keiichi
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2018, 28 (04)
  • [2] Nonproportional Low Cycle Fatigue for 316L Stainless Steel
    He Guoqiu Chen Chengshu (Department of Materials Engineering
    Southwest Jiaotong University)
    Journal of Southwest Jiaotong University, 1997, (02)
  • [3] HTS SQUID application for measuring the magnetic properties of AISI type 316L(N) steel
    Park, DG
    Kim, DW
    Hong, JH
    Timofeev, VP
    Kim, CG
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2000, 215 : 785 - 787
  • [4] Low Cycle Fatigue Behaviour of 316 LN Stainless Steel in Presence of Notch
    Richa Agrawal
    J. Veerababu
    Sunil Goyal
    R. Sandhya
    Rashmi Uddanwadiker
    Pramod Padole
    Transactions of the Indian Institute of Metals, 2016, 69 : 457 - 461
  • [5] Effect of notch on low cycle fatigue behaviour of 316 LN stainless steel
    Sunil Goyal
    J. Veerababu
    R. Sandhya
    K. Laha
    A. K. Bhaduri
    Transactions of the Indian Institute of Metals, 2016, 69 : 1015 - 1022
  • [6] Low Cycle Fatigue Behaviour of 316 LN Stainless Steel in Presence of Notch
    Agrawal, Richa
    Veerababu, J.
    Goyal, Sunil
    Sandhya, R.
    Uddanwadiker, Rashmi
    Padole, Pramod
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2016, 69 (02) : 457 - 461
  • [7] Effect of notch on low cycle fatigue behaviour of 316 LN stainless steel
    Goyal, Sunil
    Veerababu, J.
    Sandhya, R.
    Laha, K.
    Bhaduri, A. K.
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2016, 69 (05) : 1015 - 1022
  • [8] Magnetic evaluation of a solar panel using HTS-SQUID
    Kiwa, Toshihiko
    Fukudome, Yohei
    Miyazaki, Shingo
    Saari, Mohd Mawardi
    Sakai, Kenji
    Tsukada, Keiji
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2013, 494 : 195 - 198
  • [9] Effect of low cycle fatigue on subsequent high cycle fatigue life of 316L stainless steel
    Wheatley, G
    Estrin, Y
    Hu, XZ
    Brechet, Y
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 254 (1-2): : 315 - 316
  • [10] Low cycle fatigue and creep-fatigue response of the 316Ti stainless steel
    Krovvidi, S. C. S. P. Kumar
    Goyal, Sunil
    Bhaduri, A. K.
    FRATTURA ED INTEGRITA STRUTTURALE, 2019, 13 (48): : 577 - 584
12345