The Relationship between Microstructure and Fracture Behavior of TiAl/Ti2AlNb SPDB Joint with High Temperature Titanium Alloy Interlayers

被引:2
|
作者
Liao, Minxing [1 ]
Tian, Hao [1 ]
Zhao, Lei [2 ]
Zhang, Boxian [3 ]
He, Jianchao [1 ]
机构
[1] Harbin Inst Technol, Inst Special Environm Phys Sci, Shenzhen 518055, Peoples R China
[2] Cent Iron & Steel Res Inst, Dept Funct Mat Res, Beijing 100081, Peoples R China
[3] AVIC Mfg Technol Inst, Aeronaut Key Lab Welding & Joining Technol, Beijing 100024, Peoples R China
基金
中国国家自然科学基金;
关键词
spark plasma diffusion bonding; TiAl; microstructure; mechanical properties; fracture; GAMMA-TIAL ALLOYS; MECHANICAL-PROPERTIES; PURE TI; DEFORMATION; EVOLUTION; PHASE; FOIL; NB;
D O I
10.3390/ma15144849
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
In this paper, spark plasma diffusion bonding technology was employed to join TiAl and Ti2AlNb with high temperature titanium alloy interlayer at 950 degrees C/10kN/60 min, then following furnace cooling at cooling rate up to 100 degrees C/min. After welding, the joint was aging heat-treated at 800 degrees C for 24 h. The microstructure and the elements diffusion of the TiAl/Ti2AlNb joint was analyzed by field emission scanning electron microscopy (FESEM) with EDS. Moreover, the tensile properties of the joint were tested at room temperature, 650 degrees C, and 750 degrees C. The results show that the spark plasma diffusion bonding formed a high quality TiAl/Ti2AlNb joint without microcracks or microvoids, while also effectively protecting the base metal. Significant differences in the microstructure of the joint appeared from TiAl side to Ti2AlNb side: TiAl BM (Base Metal) -> DP(Duplex) and NG (Near-Gamma) -> alpha(2)-phase matrix with needle-like alpha-phase -> bulk alpha(2)-phase -> needle-like alpha-phase -> metastable beta-phase -> Ti2AlNb BM. After heat treatment at 800 degrees C for 24 h, the microstructure of the TiAl side and the interlayer region did not change, but the density and size of the needle-like alpha-phase in region 3 increased slightly. The microstructure of Ti2AlNb near the weld changed obviously, and a large number of fine O phases are precipitated from the metastable beta phase matrix after heat treatment. Except for the Ti2AlN near-interface region, the effect of heat treatment on the microstructure of the joint is not significant. The microhardness of the joint is in the shape of a mountain peak. The maximum microhardness at the interface is above 500 HV, and it is significantly reduced to 400 HV after heat treatment. The fracture of the joint occurred at the interface at room temperature, 650 degrees C, and 750 degrees C. with the tensile strength 450 MPa, 540 MPa, and 471 Mpa, respectively, and mainly showing brittle fracture.
引用
收藏
页数:14
相关论文
共 50 条
  • [41] Thermal deformation behavior and mechanism of intermetallic alloy Ti2AlNb
    Zhang, Qin-chai
    Chen, Ming-he
    Wang, Hui
    Wang, Ning
    Ouyang, Jin-dong
    Li, Xin-xiao
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2016, 26 (03) : 722 - 728
  • [42] Microstructure evolution and mechanical properties of bioinspired interpenetrating Ti2AlNb/TiAl matrix composite with a crossed-lamellar structure
    Zou, Hang
    Hu, Rui
    Zhou, Mi
    Gao, Zitong
    Liu, Xinxin
    Luo, Xian
    COMPOSITES PART B-ENGINEERING, 2024, 287
  • [43] Microstructure evolution and mechanical properties of diffusion bonding Al5(TiZrHfNb)95 refractory high entropy alloy to Ti2AlNb alloy
    Du, Y. J.
    Xiong, J. T.
    Jin, F.
    Li, S. W.
    Yuan, L.
    Feng, D.
    Shi, J. M.
    Li, J. L.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2021, 802
  • [44] Numerical Simulation of Low Cycle Fatigue Behavior of Ti2AlNb Alloy Subcomponents
    Wang, Yanju
    Zhu, Zhenyu
    Sha, Aixue
    Hao, Wenfeng
    CMES-COMPUTER MODELING IN ENGINEERING & SCIENCES, 2023, 136 (03): : 2655 - 2676
  • [45] Microstructure and property of Ti2AlNb alloy by selective electron beam melting
    Che Q.
    He W.
    Li H.
    Cheng K.
    Wang Y.
    Cailiao Gongcheng/Journal of Materials Engineering, 2022, 50 (07): : 156 - 164
  • [46] Elemental Composition, Phase Diagram, Microstructure, Fabrication Processes, and Mechanical Properties of Ti2AlNb Alloy: A Review
    Fu, Yanqi
    Su, Zimu
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (23) : 12819 - 12846
  • [47] Numerical Simulation of Fatigue Behavior of Four Ti2AlNb Alloy Structural Parts
    Zhu, Zhenyu
    Hao, Wenfeng
    Wu, Weiguo
    JOURNAL OF TESTING AND EVALUATION, 2023, 51 (05) : 3350 - 3368
  • [48] Oxidation behavior of Al/Cr coating on Ti2AlNb alloy at 900°C
    Yang, Zhengang
    Liang, Wenping
    Miao, Qiang
    Chen, Bowen
    Ding, Zheng
    Roy, Nipon
    MATERIALS RESEARCH EXPRESS, 2018, 5 (04):
  • [49] Enhanced tensile strength of TiAl/Ti2AlNb diffusion bonding joint by a novel post-bonded hot deformation
    Zhu, Lei
    Wang, Xin
    Chen, Yanglan
    Wei, Beibei
    Zheng, Guoming
    Fan, Zizhao
    Zou, Juntao
    Tang, Bin
    Li, Jinshan
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 29 : 3598 - 3605
  • [50] High temperature oxidation behaviors of Al/Cr composite coating on Ti2AlNb alloy
    Yang, Zhengang
    Liang, Wenping
    Hu, Linquan
    Zhang, Zhengwen
    Wang, He
    Chen, Bowen
    MATERIALS RESEARCH EXPRESS, 2024, 11 (01)