Microstructure and mechanical properties of HSLA-100 steel repaired by laser metal deposition

被引：37

作者：

Sun, G. F. ^{[1
]}

Yao, S. ^{[1
]}

Wang, Z. D. ^{[1
]}

Shen, X. T. ^{[1
]}

Yan, Y. ^{[1
]}

Zhou, R. ^{[2
]}

Ni, Z. H. ^{[1
]}

机构：

[1] Southeast Univ, Sch Mech Engn, Nanjing 211189, Jiangsu, Peoples R China

[2] Jiangsu Univ Sci & Technol, Sch Mech & Met Engn, Zhangjiagang 215600, Peoples R China

来源：

SURFACE & COATINGS TECHNOLOGY | 2018年 / 351卷

关键词：

Laser methods; Iron alloys; Characterization; Electron microscopy; X-ray analysis; Fracture behavior; HEAT-AFFECTED ZONE; IMPACT TOUGHNESS; STAINLESS-STEEL; PLATE STEEL; STRENGTH; ALLOY; TEMPERATURE; TECHNOLOGY; TRANSITION; COMPONENTS;

D O I：

10.1016/j.surfcoat.2018.07.048

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

HSLA-100 steel substrates with pre-machined trapezoidal grooves were repaired by laser metal deposition with HSLA-100 and nickel base alloy (GH3536) powders. The grooves can be restored and good metallurgical bonding was achieved. The microstructure and mechanical properties were analyzed. Results showed that the microstructure of the repaired zone was typical fine columnar crystals and dendrites. The main phase in the repaired zone (RZ) was martensite confirmed by transmission electron microscopy (TEM) and X-ray diffraction (XRD) results. No visible micro-pores or cracks was found under optical microscopy (OM). The micro-hardness of the RZ repaired with HSLA-100 steel powder was in the range of 240-350 HV while the sample repaired with GH3536 showed a relatively smooth micro-hardness distribution. The tensile properties were comparable to that of the substrate. The average absorbed impact energy at -40 degrees C of specimens repaired with HSLA-100 steel and GH3536 powder reached 29.6% and 88.5% that of the base material, respectively. The fracture mechanism was revealed by the SEM fracture analysis.

引用

页码：198 / 211

页数：14

共 40 条

[1] Mechanical anisotropy in Ca-treated and ultra-low sulphur HSLA-100 steel [J].

Abyazi, A. ;

Ebrahimi, A. R. .

MATERIALS SCIENCE AND TECHNOLOGY, 2016, 32 (10) :976-984

[2]

[Anonymous], 2007, WOODHEAD PUBL MATER

[3]

Belotserkovsky M., 2009, STEEL THERMAL SPRAYE, V88, p243s

[4] Repairing of sintered tools using laser cladding by wire [J].

Capello, E ;

Colombo, D ;

Previtali, B .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2005, 164 :990-1000

[5] Microstructure and mechanical properties of a thick-section high-strength steel welded joint by novel double-sided hybrid fibre laser-arc welding [J].

Chen, Yanbin ;

Feng, Jiecai ;

Li, Liqun ;

Chang, Shuai ;

Ma, Guolong .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 582 :284-293

[6] Effects of laser cladding on fatigue performance of AISI 4340 steel in the as-clad and machine treated conditions [J].

Chew, Youxiang ;

Pang, John Hock Lye ;

Bi, Guijun ;

Song, Bin .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2017, 243 :246-257

[7] Rapid manufacturing of metal components by laser forming [J].

Costa Santos, Edson ;

Shiomi, Masanari ;

Osakada, Kozo ;

Laoui, Tahar .

INTERNATIONAL JOURNAL OF MACHINE TOOLS & MANUFACTURE, 2006, 46 (12-13) :1459-1468

[8] Structure and properties of an ultra low carbon HSLA forging [J].

Das, S ;

Ghosh, A ;

Chatterjee, S ;

Ramachandrarao, P .

SCANDINAVIAN JOURNAL OF METALLURGY, 2004, 33 (04) :203-210

[9] Weldability and microstructural aspects of shielded metal arc welded HSLA-100 steel plates [J].

Dhua, SK ;

Mukerjee, D ;

Sarma, DS .

ISIJ INTERNATIONAL, 2002, 42 (03) :290-298

[10] Influence of tempering on the microstructure and mechanical properties of HSLA-100 steel plates [J].

Dhua, SK ;

Mukerjee, D ;

Sarma, DS .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2001, 32 (09) :2259-2270

← 1 2 3 4 →