Microstructures and mechanical properties of an Al-Cu-Li-Mg-Zr alloy containing Zn and Mn

被引：2
|
作者：
Chen, Yong-Lai [1 ]
Li, Jin-Feng [2 ]
Zhang, Yu-Wei [1 ]
Zheng, Zi-Qiao [2 ]
机构：
[1] Aerosp Res Inst Mat & Proc Technol, Beijing 100076, Peoples R China
[2] Cent South Univ Technol, Sch Mat Sci & Engn, Changsha 410083, Peoples R China
来源：
2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM | 2007年 / 546-549卷
关键词：
microstructure; mechanical property; heat treatment; Al-Cu-Li-Mg-Zr alloy;
D O I：
10.4028/www.scientific.net/MSF.546-549.995
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
An AI-3.43Cu-1.28Li-0.49Mg-0.12Zr containing 0.62Zn and 0.29Mn was designed and the microstructures and mechanical properties of the alloy with various heat treatments were investigated. The precipitates of the alloy consist of T1 (Al2CuLi), theta' (Al2Cu), a (Al5Cu6Mg2) and delta' (Al3Li). As solution temperature is changed from 485 degrees C to 530 degrees C, the solution degree of alloying elements in alloy increased, the amount of T1 in the alloy aged at 160 degrees C for 18 h increased and that of theta' is decreased, resulting in an increase of strength. After solution treatment at 530 degrees C, the alloy aged for 18 h at 145 degrees C is mainly strengthened by G P zones, and a little amount of T1 precipitates. As aging temperature is increased to 160 degrees C and 175 degrees C, the strength increased, due to the sufficient precipitation of sigma and T1. The smaller amount of T1 in the alloy aged at 190 degrees C is consistent with its lower strength. Meanwhile, it is found that the a precipitate does not coarsen as aging temperature increases in the range from 160 degrees C to 190 degrees C.
引用
收藏
页码：995 / +
页数：2
相关论文
共 50 条
  • [31] Microstructures and fatigue behavior of Al-Cu-Mg alloy containing Zr
    School of Materials Science and Engineering, Central South University, Changsha 410083, China
    Zhongguo Youse Jinshu Xuebao, 2009, 1 (50-55):
  • [32] Effect of Precipitations on Microstructures and Mechanical Properties of Nanostructured Al-Zn-Mg-Cu Alloy
    Chen, Hanbin
    Yang, Bin
    MATERIALS TRANSACTIONS, 2008, 49 (12) : 2912 - 2915
  • [33] Texture and Anisotropy of the Mechanical Properties of an Al-Mg-Li-Zn-Sc-Zr Alloy
    Il'in, A. A.
    Zakharov, V. V.
    Betsofen, M. S.
    Osintsev, O. E.
    Rostova, T. D.
    RUSSIAN METALLURGY, 2008, (05): : 406 - 412
  • [34] The structure transformation in an Al-Li-Zn-Mg-Cu-Zr alloy
    Gu, YJ
    Wahab, A
    Huang, Z
    Zhang, YG
    Chen, CQ
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 316 (1-2): : 39 - 45
  • [35] Homogenization treatment of an Al-Li-Cu-Mg-Mn-Zr alloy
    Wei, Xiuyu
    Zheng, Ziqiao
    Chen, Qiuni
    Fu, Xin
    2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 719 - +
  • [36] Effect of Sc addition on microstructures and mechanical properties of Al-Zn-Mg-Cu-Zr alloys
    Dai Xiaoyuan
    Xia Changqing
    Liu Changbin
    RARE METAL MATERIALS AND ENGINEERING, 2006, 35 (06) : 913 - 916
  • [37] Characterization of microstructure and mechanical properties of Al-Cu-Mg-Ag-(Mn/Zr) alloy with high Cu:Mg
    Zhang, Jian Bo
    Zhang, Yong An
    Zhu, Bao Hong
    Liu, Rui Qing
    Wang, Feng
    Liang, Qi Ming
    MATERIALS & DESIGN, 2013, 49 : 311 - 317
  • [38] Microstructures and mechanical properties of Mg-Ce-Zn-Zr wrought alloy
    Wu, WH
    Xia, CQ
    JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2004, 11 (04): : 367 - 370
  • [39] Microstructures and mechanical properties of Mg-Ce-Zn-Zr wrought alloy
    Wen-hua Wu
    Chang-qing Xia
    Journal of Central South University of Technology, 2004, 11 : 367 - 370
  • [40] Effects of Retrogression and Re-aging Treatment on Microstructures and Mechanical Properties of Ultrahigh Strength Al-Zn-Mg-Cu-Zr Alloy Containing Sc
    Li Wenbin
    Pan Qinglin
    Liu Junsheng
    Liang Wenjie
    Liu Xiaoyan
    He Yunbin
    RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (09) : 1646 - 1650
12345