Microstructure and Properties of Semi-Solid Extrusion of AlSi7Mg Alloy

被引：0

作者：

Zhao Da-zhi ^{[1
]}

Liang Hai-cheng ^{[2
]}

Liu Fang ^{[1
]}

Yu Fu-xiao ^{[1
]}

机构：

[1] Northeastern Univ, Key Lab Electromagnet Proc Mat, Shenyang 110004, Peoples R China

[2] E China Univ Sci & Technol, Sch Resources & Environm Engn, Shanghai 200237, Peoples R China

来源：

JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL | 2010年 / 17卷

关键词：

semi-continuous casting; AlSi7Mg alloy; forward-extrusion; microstructure and properties; BEHAVIOR;

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The semi-solid forward-extruding feasibility of AlSi7Mg alloy cast by low-superheat semi-continuous casting process was studied through analyzing the microstructures and properties of the forward-extruded bars. The results show that the semi-solid forward-extruded bars of the AlSi7Mg alloy billet, cast by low-superheat semi-continuous casting process, are facial-smoothed, microstructure-fined and homogeneous. The feasibility of semi-solid forward-extrusion of AlSi7Mg alloy is perfect. Treated by the solution at 540 degrees C for 5 hours and aging at 175 degrees C for 10 hours, the tensile strength of the extruded bars is above 320 MPa and the elongation rate is above 11.43%.

引用

页码：56 / 61

页数：6

共 17 条

[1]

AJIBOYE JS, 2007, INT J MECH SCI

[2]

Altenpohl D G, 1996, ALUMINUM, P694

[3]

ALTINBALIK T, 2007, MAT DESIGN

[4]

DING HL, 2007, J ALLOYS COMPOUNDS

[5] Liquidus semi-continuous casting, reheating and thixoforming of a wrought aluminum alloy 7075 [J].

Dong, J ;

Cui, JZ ;

Le, QC ;

Lu, GM .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 345 (1-2) :234-242

[6]

FLEMING MC, 2006, P 9 INT C SEM PROC A, P1

[7] Shear deformation behavior of Al-5% Mg in a semi-solid state [J].

Iwasaki, H ;

Imori, T ;

Mabuchi, M ;

Higashi, K .

ACTA MATERIALIA, 1998, 46 (18) :6351-6360

[8] The effect of strain rate on macroscopic behavior in the compression forming of semi-solid aluminum alloy [J].

Kang, CG ;

Choi, JS ;

Kim, KH .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1999, 88 (1-3) :159-168

[9] Feasibility of metal forming in semi-liquid state [J].

Lapkowski, W ;

Sinczak, J ;

Rusz, S .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1997, 63 (1-3) :260-264

[10]

LEWANDOWSKI MS, ACTA MAT, V47, P4695

← 1 2 →