Aluminum-graphite composite produced by mechanical milling and hot extrusion

Aluminum-graphite composites were produced by mechanical milling followed by hot extrusion. Graphite content was varied between 0 and 1 wt.%. Al-graphite mixtures were initially mixed in a shaker mill without ball, followed by mechanical milling in a High-energy simoloyer mill for 2 It under argon atmosphere. Milled powders were subsequently pressed at similar to 950 MPa for 2 min, and next sintered under vacuum for 3 It at 823 K. Finally, sintered products were held for 0.5 h at 823 K and hot extruded using indirect extrusion. Tension and compression tests were carried out to determine the yield stress and maximum stress of the materials. We found that the mechanical resistance increased as the graphite content increased. Microstructural characterization was done by transmission electron microscopy. Al-O-C nanofibers and graphite nanoparticles were observed in extruded samples by transmission electron microscopy. These nanoparticles and nanofibers seemed to be responsible of the reinforcement phenomenon. (C) 2006 Elsevier B.V. All rights reserved.